【摘 要】
：
A novel Ti cored wire containing TiB2,Al60V40 and Ti6Al4V mixed powders was developed for wire-feed arc deposition of TiB/Ti composite coating,to enhance the hardness and wear resistance of Ti alloy.Results showed that after experiencing several chemical
【机 构】
：
School of Materials Science and Engineering,Harbin Institute of Technology,Harbin,150001,PR China;St
论文部分内容阅读
A novel Ti cored wire containing TiB2,Al60V40 and Ti6Al4V mixed powders was developed for wire-feed arc deposition of TiB/Ti composite coating,to enhance the hardness and wear resistance of Ti alloy.Results showed that after experiencing several chemical reactions,the wire was melted in the arc zone and turned into nonuniform droplets composed of Ti-Al-V-B melt and undecomposed TiB2 particles.With the increase of welding current,the detachment time of droplet shortened while the transfer frequency accelerated,accompanied by the improvement in coating surface quality.The spatial distribution of TiB whiskers in coating was governed by welding current.A uniform distribution could be achieved as welding current was sufficient at the expense of elevated dilution ratio,while increasing wire feeding speed could compensate the dilution loss of TiB whisker to some extent.The decomposition process of TiB2 particles and the microstructure evolution mechanism of coating was discussed in detail.The optimum coating possessed uniform microstructure,relatively low dilution ratio,and high hardness(639.1 HV0.5)as compared with Ti6Al4V substrate(326 HV0.5).Indentation morphology analysis verified the excellent performance was ascribed to the load-sharing strengthening of TiB whiskers.This study provides a high-efficiency fabrication method for the ever-developing titanium matrix composites(TMCs)coating.
其他文献
Lattice thermal conductivities of zirconium carbide(ZrCx,x=1,0.75 and 0.5)ceramics with different car-bon vacancy concentrations were calculated using a combination of first-principles calculations and the Debye-Callaway model.The Grüneisen parameters,Deb
FCC,BCC and B2 phases,the most common phases in high-entropy alloys(HEAs),are widely investigated to tailor their mechanical and magnetic performances.The detailed investigation of FCC to BCC/B2 phase transformation of AlCoCrFeNi HEA in this paper reveals
Chemo-resistance has pushed cancer treatment to the boundary of failure.This challenge has encouraged scientists to look for nanotechnological solutions.In this study,we have taken this goal one step further without depending on chemotherapy.Specifically,
The understanding of temperature and time-dependent metal borides precipitation/dissolution is cru-cial for the design of the transient liquid phase(TLP)bonding process of Ni-based alloys.It however remains elusive despite substantial research efforts for
Severe plastic deformation is known to induce grain refinement and gradient structure on metals\'sur-faces and improve their mechanical properties.However,the fundamental mechanisms behind the grain refinement and micromechanical properties of materials
There is currently a gap in our understanding of mechanisms that contribute to high strength and high plasticity in high strength UFG ferritic steel with nano-size Fe3C carbides in situations that involve com-bination of various strain rates and high temp
9Cr3W3CoB steels are developed to serve at the temperature range of 620-650℃,and have been recog-nized as the most promising martensitic heat-resistant steels for supercritical power plants.Due to the high W and Co contents,the Fe2W Laves phase in such 9C
Deformation-induced hcp nano-lamellae with various widths and interspacings were observed in the CoCrNi medium-entropy alloy(MEA)under high strain rate and cryogenic temperature in the present study.Higher hardness was found in the cryogenic-deformed samp
In this work,the microstructure evolution,thermal expansion,thermal conductivity,and thermal shock resistance properties of the plasma-sprayed X1-Gd2SiO5,X2-Y2SiO5,and X2-Er2SiO5 coatings were eval-uated and compared by experimental measurement and theore
Metal phthalocyanine is considered one of the most promising candidates for the design and fabrication of flexible resistive random access memory(RRAM)devices due to its intrinsic flexibility and excel-lent functionality.However,performance degradation an