An Evaluation Method for Combustion Characteristics of Coal in Cement Industry
【机 构】
:
School of Environmental Science and Engineering, Tianjin University, Tianjin 300072, China;Tianjin C
【出 处】
:
武汉理工大学学报(材料科学版)(英文版)
【发表日期】
:
2010年1期
其他文献
Prediction of Mechanical Properties of 50CrVA Tem-pered Steel Strip for Horn Diaphragm Based on BPAN
50CrVA cold-rolled spring steel strip was used to fabricate the diaphragm of the automotive horn.The material parameters which were taken into account in the design of the dia-phragm involve elongation,elastic limit,Young\'s modulus,yield strength and t
Particle reinforced Sn-Zn based composite solders were obtained by adding Cu powders to Sn-9Zn melts. The microstructure analysis reveals that in situ Cu_5Zn_8 particles are formed and distributed uniformly in the composite solders. The strength and plast
Red mud was activated to be a mineral admixture for Portland cement by means of heating at different elevated temperatures from 400 ℃ to 700 ℃. Results show that heating was ef-fective, among which thermal activation of red mud at 600 ℃ was most effective
Astabilizedsoilstructureformation model wasintroduced. In ordertoformcompact stabilized soil structure, cementitious hydrates were needed to wrap and bind the soil aggregates.Meanwhile, expansible hydrates were needed to squeeze and fill the pores, especi
Degradation of Pore Structure and Microstructures in Hardened Cement Paste Subjected to Flexural Loa
Hardened cement paste was subjected to the flexural loading and wet-dry cycles in sea water.The degradation of microstructures was obtained using scanning electron microscope(SEM),and the energy dispersive spectrum(EDS)analysis was carried to analyze the
A new type of cement was prepared with ground limestone powder,blastfurnace slag,steel slag and gypsum without calcination.The fraction of ground limestone powder in the cement was as high as 40 wt%-60 wt%without Portland clinker.All of its physical prope