论文部分内容阅读
A solid-solution-phase Ba1.75Ca1.25MgSi2O8: Eu2 , Mn2 phosphor in the photosynthetic action spectrum with dual band emissions at 438 nm and 660 nm is fabricated. X-ray diffraction (XRD) confirms the presence of the solid-solution phase. With the supporting information from the diffuse reflection spectrum, a feasible way to obtain higher energy-transfer (ET) efficiency is attained, and the ET efficiency of Eu2 –Mn2 is enhanced to 76%. The mechanism of this enhancement is owing to variation of the solid solution composition of Ca3MgSi2O8 and Ba3MgSi2O8, which contributes to the extension of the critical distance. Temperature-dependent results show an enhancement which is attributed to Ca. These enhancements show great promise for improving eco-lighting devices.