The thermodynamic analysis of the formation of in-situ reinforced phases in(TiB 2 +Al 3 Ti)/Al- 4.5Cu composites prepared by mixed salts reaction was conducted,and heat changes of mixed salts system were analyzed by differential thermal analysis(DTA).The results show that although TiB 2 possesses the strongest formation ability in Al-Ti-B ternary system,[Ti]is relatively excessive in the in-situ reaction and it combines with Al to form Al 3 Ti phase.The reinforced phases are TiB 2 and Al 3 Ti in the produced composites due to the reaction taking place to form reinforced phase with the addition of mixed salts into Al-4.5Cu melt between 900 ℃and 1 032℃.
The thermodynamic analysis of the formation of in-situ reinforced phases in (TiB 2 + Al 3 Ti) / Al- 4.5Cu composites prepared by mixed salts reaction was conducted, and heat changes of mixed salts system were analyzed by differential thermal analysis (DTA ) The results show that although TiB 2 possesses the strongest formation ability in Al-Ti-B ternary system, [Ti] is relatively excessive in the in situ reaction and it combines with Al to form Al 3 Ti phase. The reinforced phases are TiB 2 and Al 3 Ti in the produced composites due to the reaction taking place to form reinforced phase with the addition of mixed salts into Al-4.5Cu melt between 900 ° C and 1 032 ° C.