With the help of an electromagnetic stirring device self-made and alloy melt quenching technology,the effect of electromagnetic stirring parameters on the micro
【机 构】
：
School of Materials Science and Engineering
论文部分内容阅读
With the help of an electromagnetic stirring device self-made and alloy melt quenching technology,the effect of electromagnetic stirring parameters on the microstructures of semi-solid AZ91D alloy was mainly studied at the stirring frequency of 200 Hz.The experimental results show that when the stirring power rises,the primary α-Mg rosettes in the semi-solid melt will bear stronger man-made temperature fluctuation and the root remelting effect of the dendritic arms is promoted so that the spherical primary α-Mg grains become much more and rounder.If the stirring frequency is 200 Hz,the ideal semi-solid microstructure of AZ91D magnesium alloy can be obtained when the stirring power is increased to 6.0 kW.If the stirring frequency is 200 Hz and the stirring power is 6.0 kW,it is found that the lower cooling rate is favorable for the spherical primary α-Mg grains to be developed during the electromagnetic stirring stage.If the AZ91D magnesium alloy billet prepared during electromagnetic stirring at the stirring frequency of 200 Hz and the stirring power of 6.0 kW is reheated to the solidus and liquidus temperature region,the primary α-Mg grains shape will get more spherical,so it is very advantageous to the semi-solid thixoforming process.
其他文献
The residual stresses on the surface of the differently ground and polished silicon nitride ceramics were measured using X-ray diffraction and identified by SEM
The main cause to the deactivation of ZSM-5 catalyst, used for oxidation of benzene to phenol (BTOP)by nitrous oxide, is that the carbon deposition on the catal
Homogeneous HA coating materials were prepared on porous titanium by the low-temperature combustion synthesis. It was found that the mechanical properties of th
A novel bifunctional dye containing spirobenzopyran and cinnamoyl moiety has been prepared and its photochromic behavior following irradiation at different wave
The bioactive α-Ca3 (PO4)2 bone cement was studied by XRD , SEM and isothermal calorimetric measurements. The results showed that a mixed pattern of TCP and hy
The bonding of solid steel plate to liquid aluminum was studied using rapid solidification. The relationship models of interfacial shear strength and thickness
The aim of this work was to produce a nanoscale fluoridated and potassium containing hydroxyapatite via sol-gel method and to observe the effect of occlusion of
Three cement samples were prepared, including OPC consisted of 100wt% portland cement, PFA consisted of 70wt% portland cement and 30wt% fly-ash, and CA consiste
In recent years,materials with ultrafine grain size(UFG) have attracted much attention.By using severe plastic deformation(SPD) techniques,materials with fine g
The distribution of microelement Fe, Si, Cu and Mg in the surface layer of aluminum foil annealed at 300℃ and 500℃ were determined by secondary ion mass spect