The in situ synthesized MoSi2-SiC composite is proved to be of higher fracture tough-ness than the monolithic MoSi2. The TEM and HREM study reveals that the int
Under the condition of die casting and reheating temperature of 570-580° C, the Rhe-ological behavior of semi-solid aluminum alloy (A356) is pseudoplastici