研究了00Cr26Ni6Mo4CuTiAl不锈钢的焊接性及其焊接工艺问题,在熔敷金属强度低于母材的情况下,预热到200℃,以低的线能量(0.78kJ/mm)施焊,可以得到无裂纹的焊接接头;其机械性能略低于母材,热影响区的耐点蚀性能与母材相当.
The weldability and welding process of 00Cr26Ni6Mo4CuTiAl stainless steel were studied. When the deposited metal strength is lower than that of the base metal, preheated to 200 ℃ and welded with low line energy (0.78kJ / mm) Crack welded joints; its mechanical properties slightly lower than the base metal, heat-affected zone pitting corrosion resistance and base metal equivalent.