【摘 要】
：
研究了高锰钢离心铸造的生产流程,消除了离心铸造ZG120Mn13衬套的缩孔、缩松等缺陷,离心铸造ZG120Mn13钢组织致密,晶粒尺寸在70~130μm之间,晶粒度为3~4级。生产结果表明,ZG1
【机 构】
：
青岛港湾职业技术学院机械系,青岛蓝鼎华昆耐磨钢有限公司,
论文部分内容阅读
研究了高锰钢离心铸造的生产流程,消除了离心铸造ZG120Mn13衬套的缩孔、缩松等缺陷,离心铸造ZG120Mn13钢组织致密,晶粒尺寸在70~130μm之间,晶粒度为3~4级。生产结果表明,ZG120Mn13衬套生产工艺由砂型铸造改为离心铸造后,成品率提高了35%,铸造生产率提高了40%,成本下降了约26%。
The production process of high manganese steel centrifugal casting was studied. The defects such as shrinkage cavity and shrinkage of centrifugal casting ZG120Mn13 bushing were eliminated. The centrifugal casting ZG120Mn13 steel was compact in structure, the grain size was between 70 ~ 130μm and the grain size was 3 ~ level 4. Production results show that, ZG120Mn13 bush production process changed from sand casting to centrifugal casting, the yield increased by 35%, casting productivity increased by 40%, the cost decreased by about 26%.
其他文献
研究了不同含量的Ti和Mg对消失模铸造Al-Cu合金组织和力学性能的影响。结果表明,当Ti含量从0.3%提高至0.9%和1.2%时,其脆性相含量增多且组织形态逐渐粗大,Al-Cu合金的抗弯强
利用无线Mesh网多跳传输、灵活组网的特点和VoIP通信性能良好且资费低廉的优势,构建基于无线Mesh网的VoIP通信系统,通过应用层性能测试软件IxChariot对系统的整体性能进行了
主要介绍了近几年出现的超宽带滤波器设计和实现技术.这些滤波器具有很多的优点,包括小尺寸、高矩形度、低损耗、好的线性特性和容易实现的陷波功能.这些性能优良的滤波器采
数学和我们的生活息息相关，这不，某街心花园正在设计绿化带，设计草图如下图所示，阴影部分表示绿化带。你能求出绿化带的面积吗？ 方法一： 先用一条虚线把阴影部分拆分成两个图形，再把左边的图形向左旋转90°。 这时我们得到了两个一样的图形，计算阴影面积就变得简单多了，即计算半圆面积减去三角形面积再乘2，列式如下： 3.14×（5×5）× -10×5× ×2 方法二： 我們直接把左边的图形向左
目的 探讨方丝弓矫治术对前牙外伤固定治疗的效果.方法 62例前牙外伤患者,其中38例应用方丝弓矫治器固定外伤前牙,24例采用金属丝牙弓夹板固定治疗,时间4～6周.比较2组疗效.结果 治疗后1年追踪复查,方丝弓治疗总有效率91.49%,而金属丝牙弓夹板组总有效率为70.49%,2组比较差异有统计学意义(P＜0.01).结论 方丝弓矫治器固定治疗前牙外伤疗效满意、可靠,值得推广。
目的 研究探讨滚法在治疗软组织损伤中的机理.方法 参照丁季峰的滚法手法.结果推拿滚法具有疏经通络,行气活血;解除痉挛,松解粘连;理顺筋脉,滑利关节的作用.
随着嵌入式技术的快速发展,嵌入式多媒体技术的应用越来越多,可视对讲作为人与人之间的一种沟通方式,其在嵌入式产品上的应用有着迫切需求。在FIC8120嵌入式平台上移植和构建
亚低温方法成功治疗重型颅脑损伤已被诸多基础研究和临床病例所证实[1]亚低温能显著减轻脑损伤后神经功能障碍和脑病理形态损害,保护血脑屏障功能,从而降低颅脑损伤患者的病
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
在语音合成领域,大语料库拼接合成方式有一些固有弱点,例如语料库建设成本过高,合成稳定性差等.而基于隐马尔可夫模型(HMM)的语音合成技术在多样化语音合成、多语言支持、系