The superconductivity of iron-based superconductor SmO 0.7 F 0.2 FeAs was investigated. The SmO 0.7 F 0.2 FeAs sample was prepared by the two-step solid-state reaction method. The onset resistivity transition temperature is as high as 56.5 K. X-ray diffraction (XRD) results show that the lattice parameters a and c are 0.39261 and 0.84751 nm, respectively. Furthermore, the global J c was more than 2.3 × 10 5 A/cm 2 at T = 10 K and H = 9 T, which was calculated by the formula of J c = 20ΔM/[a(1-a/(3b))]. The upper critical fields, H c2 ≈ 256 T (T = 0 K), was determined according to the Werthamer-Helfand-Hohenberg formula, indicating that the SmO 0.7 F 0.2 FeAs was a superconductor with a very promising application.
The superconductivity of iron-based superconductor SmO 0.7 F 0.2 FeAs was investigated. The SmO 0.7 F 0.2 FeAs sample was prepared by the two-step solid-state reaction method. The onset resistivity transition temperature was as high as 56.5 K. X-ray diffraction (XRD) results show that the lattice parameters a and c are 0.39261 and 0.84751 nm, respectively. Furthermore, the global J c was more than 2.3 × 10 5 A / cm 2 at T = 10 K and H = 9 T, which was calculated by the formula of J c = 20ΔM / [a (1-a / (3b))]. The upper critical fields, H c2 ≈ 256 T (T = 0 K), was determined according to the Werthamer-Helfand- Hohenberg formula, indicating that the SmO 0.7 F 0.2 FeAs was a superconductor with a very promising application.