TiO2 and N-doped TiO2 films were deposited on the glass substrates by arc ion plating method. The results show that the deposition rate does not change with the
The composite metastable(Ti0.5Al0.5)N,(Ti0.45Al0.45Cr0.1)N and(Ti0.35Al0.35Cr0.3)N coatings were respectively deposited on a wrought martensite steel 1Cr11Ni2W2
The pressing bonding of steel plate to QTi3.5 3.5graphite slurry was studied. The bonding conditions were 620 ℃ for preheating temperature of steel plate, 530