论文部分内容阅读
锑(之二) 四、锑化物光导电导纤维 1.光导纤维材料 (1)含Sb_2O_370,PbCl_330克分子％的混合物在600—800℃氮气气氛下加热熔化成氧氯化物玻璃。这种玻璃具有便于加工成片或丝的热特性,宜作红外光传导材料。 (2)(Ge0.42S0.58)_1-x (Sb0.4 S0.6)_x类型的硫族化物玻璃,含锑复合卤化物玻璃或两者联合也可作高效率、低光耗的光导纤维材料。 (3)As-Ge-Sb硫族化物玻璃毛细管(外径300—500微米,内径100—300微米),轻巧柔软,用于CO_2激光体可见激光传输。 (4)SnO_2,Sb_2O_3,In_2O_3金属氧化物熔化拉丝,表面涂以有机材料涂层,也是一种光导纤维。
Antimony (二) 四, Antimonide Photoconductive Conductive Fiber 1. Optical Fiber Material (1) The mixture containing Sb2O3, PbCl3 and 300 mol% of the molecule is heated and melted into oxychloride glass under a nitrogen atmosphere of 600-800 deg.c. This glass has easy to process into a sheet or silk thermal characteristics, suitable as infrared light-conducting materials. (2) (Ge0.42S0.58) _1-x (Sb0.4 S0.6) _x type chalcogenide glass, antimony-containing composite halide glass or both can also be used as a high efficiency, low light consumption of the light guide Fiber material. (3) As-Ge-Sb chalcogenide glass capillaries (outer diameter 300-500 μm, inner diameter 100-300 μm), light and soft for visible laser transmission of CO 2 laser. (4) SnO_2, Sb_2O_3, In_2O_3 metal oxide melt drawing, the surface coated with a coating of organic materials, but also an optical fiber.