【摘 要】
：
利用真空感应熔炼的方法制备出(ZrTi)V2合金,在950℃下对合金进行长时间的退火处理,对合金的相结构及吸氢性能进行测试。结果表明:(ZrTi)V2合金主要由C15Laves相、α-Zr相、Z
【机 构】
：
西北工业大学凝固技术国家重点实验室,
论文部分内容阅读
利用真空感应熔炼的方法制备出(ZrTi)V2合金,在950℃下对合金进行长时间的退火处理,对合金的相结构及吸氢性能进行测试。结果表明:(ZrTi)V2合金主要由C15Laves相、α-Zr相、Zr3V3O相和V基固溶体相组成,热处理使得α-Zr相及V基固溶体相减少;该合金经400℃,1h除气之后,再经过一次吸放氢循环即可达到最佳的活化效果;根据Van’tHoff关系外推出室温下该合金的平衡压力为8.1×10-14Pa。
The (ZrTi) V2 alloy was prepared by vacuum induction melting and the alloy was annealed at 950 ℃ for a long time. The phase structure and hydrogen absorption properties of the alloy were tested. The results show that the (ZrTi) V2 alloy mainly consists of C15Laves phase, α-Zr phase, Zr3V3O phase and V-based solid solution phase. The α-Zr phase and V-based solid solution phase decrease with heat treatment. , And then through a cycle of hydrogen absorption and absorption to achieve the best activation effect; according to Van’tHoff relationship at room temperature, the equilibrium pressure of the alloy was 8.1 × 10-14Pa.
其他文献
将硒粉和铌粉按一定化学计量比混合,随后在800℃下固相反应生成NbSe2粉末;将得到的NbSe2粉末与一定量的Cu粉在QMISP2型球磨机上球磨9 h(转速200 r·min-1)混合均匀,干燥后放
一、肾血管性高血压45例研究结果: ①45例患者中有34例血浆肾素活性增高,其中双侧肾动脉狭窄的患者比单侧肾动脉狭窄的患者要少。②把血浆肾素与同时测得的血压值进行比较,
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥
The effects of differential speed rolling (DSR) on the texture of AZ31B magnesium alloy sheets were investigated,which were achieved by tailoring deformation te
目的掌握本溪市蚊类种群构成及分布,为指导蚊虫防治提供科学依据。方法采取灯诱法对本溪市居民区、医院、公园3种场所的蚊密度进行监测。结果 2001-2010年本溪市住区蚊类种群
滑县位于河南省东北部,地处豫北古黄河冲积平原,位于农业部优势农产品区域布局规划“优质花生规划区”内,是河南省中大果花生主产区之一.为加快产业结构调整,推进滑县花生生
第二次世界大战之后科学全面步入了普莱斯所说的大科学时代。大科学时代科学研究的最大特征在于科学研究靡费不低。步入新世纪，科学所耗费的经费更是越来越多，欧洲大型粒子对撞
报告斯里兰卡65例初发疟疾,62例为间日疟,3例恶性疟。外周血片均找到疟原虫。红细胞原虫感染率0.1～2％。全部病例均有发热,但无并发症。 37例(57％)肝脏肿大,其中10例肝脏于右肋
粘土钒矿是一类重要的钒资源。某粘土钒矿的性质分析表明,粘土钒矿的主要化学组分为SiO2,Al2O3,属酸性矿石,适宜采用硫酸浸出;其中的钒以低价不溶的V(Ⅲ)为主,大部分赋存于伊