【摘 要】
：
如所周知,在球墨铸铁件的表面上,偶而会有1毫米厚的片状石墨层,人们将这种现象归因於铁水与铸型材料以及型芯粘结剂的作用,特别是与磷甲苯磺酸硬化剂的作用结果。但是,F.马
论文部分内容阅读
如所周知,在球墨铸铁件的表面上,偶而会有1毫米厚的片状石墨层,人们将这种现象归因於铁水与铸型材料以及型芯粘结剂的作用,特别是与磷甲苯磺酸硬化剂的作用结果。但是,F.马丁(F.Martin)和S.I.卡赛(S.I.Karsay)在大断面球墨铸铁件上发现的片状石墨区域要宽得多,而且它几乎都出现在铸件的下部,并向上延伸达25毫米以上。进一步研究得出的结果是:
As is known, on the surface of a ductile iron piece there is occasionally a 1 mm thick flake graphite layer which is attributed to the effect of the molten iron on the mold material and the core binder, in particular with phosphorus Toluene sulfonic acid curing agent results. However, the area of flake graphite found on large section ductile iron castings by F. Martin and SI Karsay is much wider, and almost all of it appears in the lower part of the casting and extends up to 25 millimeters or more. The result of further research is:
其他文献
过渡金属原子簇大多以多面体的形式存在。关于它们的分子构型和成键特征,有多种理论方法和解决途径。本文主要从多面体骨架电子对理论(Polyhedral Skeletal Electron Pair T
以创新精神为核心的科学教育已成为当今教育界的热门话题。本文在理解科学创造力内涵的基础之上,从心理学视角分析了影响中学生科学创造力的各种因素,并就此探讨了它给我们的
对以三乙胺为模板剂的APO-5、SAPO-5型分子筛样品进行了水蒸气处理和酸处理。采用无定形强度卡方法分离样品中结晶相的衍射强度和无定形相的相干散射强度,测定了样品处理前后
2·1 引言纯铁是强度很低的材料,而钢材提供的强度范围很宽,从低屈服强度(约200MNm~(-2))直到极高屈服强度(约2000MNm~(-2))应有尽有。通常为获得所需的机械性能,复合使用了
本刊在1986年第2期刊登了《对化学反应中△H~0和△G~0单位的探讨》一文。该文对目前在国内外常见的物理化学及普通化学教材中△H~0和△G~0两个物理量单位的不同进行了讨论,并
薄层色谱在基础有机化学制备实验中的应用主要是定性分析物质的成份;随时间掌握反应进程,准确发现存在的问题,为做好实验提供简便易行的分析手段。下面举例说明。 (一)监测
我是个老年钓鱼爱好者,非常想学会台钓技术。但是,台钓用的钓具和装备是配套的,一时难以配齐。就是配齐了,也很沉重,老年人携带不方便。同时,台钓的灵敏度很高,老年人视力不
日本三菱电机制造公司继1976年正式生产冷轧钢板非接触式板形检测装置之后,最近又研制成功一种同时具有板形检测值绝对值化处理和板形控制功能简化的插件式《MELPLAC》型板形
用扫描俄歇探针、扫描电镜及硬度测量等方法研究了4.2Mo-0.4C-0.06P钢中晶间析出和晶间脆性。结果表明:此钢在500～700℃回火存在二次硬化现象和高晶闻脆性,且晶间脆性与晶界上
许多工业用的金属材料,如低碳钢、低合金钢、钛合金等,均具有韧-脆转移的过程,对这一转移过程的本质及其影响因素的研究,一直受到极大的重视。 金属的韧-脆转移过程受材料的