The effects of MgO and TiO_2 on the viscosity, activation energy for viscous flow, and break-point temperature of titanium-bearing slag were studied. The correlation between viscosity and slag structure was analyzed by Fourier transform infrared(FTIR) spectroscopy. Subsequently, main phases in the slag and their content changes were investigated by X-ray diffraction and Factsage 6.4 software package. The results show that the viscosity decreases when the MgO content increases from 10.00wt% to 14.00wt%. Moreover, the break-point temperature increases, and the activation energy for viscous flow initially increases and subsequently decreases. In addition, with increasing TiO_2 content from 5.00wt% to 9.00wt%, the viscosity decreases, and the break-point temperature and activation energy for viscous flow initially decrease and subsequently increase. FTIR analyses reveal that the polymerization degree of complex viscous units in titanium-bearing slag decreases with increasing MgO and TiO_2 contents. The mechanism of viscosity variation was elucidated. The basic phase in experimental slags is melilite. Besides, as the MgO content increases, the amount of magnesia–alumina spinel in the slag increases. Similarly, the sum of pyroxene and perovskite phases in the slag increases with increasing TiO_2 content. The effects of MgO and TiO_2 on the viscosity, activation energy for viscous flow, and break-point temperature of titanium-bearing slag were studied. The correlation between viscosity and slag structure was analyzed by Fourier transform infrared (FTIR) spectroscopy. phases in the slag and their content changes were investigated by X-ray diffraction and Factsage 6.4 software package. The results show that the viscosity decreases when the MgO content increases from 10.00 wt% to 14.00 wt%. , and the activation energy for viscous flow initially increases and the decreased decreases. In addition, with increasing TiO 2 content from 5.00 wt% to 9.00 wt%, the viscosity decreases, and the break-point temperature and activation energy for viscous flow initially decrease and subsequently FTIR analyzes reveal that the polymerization degree of complex viscous units in titanium-bearing slag decreases with increasing MgO and TiO_2 contents. The mechanism of viscosity variation was elucidated. The basic phase in experimental slags is melilite. In addition, as the MgO content increases, the amount of magnesia-alumina spinel in the slag increases. Similarly, the sum of pyroxene and perovskite phases in the slag increases with increasing TiO_2 content.