【摘 要】
：
Ba0.6Sr0.4TiO3 (BST) thin films were fabricated on Pt coated Si (100) substrates by sol-gel techniques with molar ratio of (Ba+Sr) to Ti changing from 0.76 to 1
【机 构】
：
School of Materials Science and Engineering
论文部分内容阅读
Ba0.6Sr0.4TiO3 (BST) thin films were fabricated on Pt coated Si (100) substrates by sol-gel techniques with molar ratio of (Ba+Sr) to Ti changing from 0.76 to 1.33. The effect of (Ba+Sr)/Ti ratio deviating from the stoichiometry on microstructure,grain growth,dielectric and tunable properties of BST thin films were investigated. TiO2 and (Ba,Sr)2TiO4 were found as a second phase at the ratios of 0.76 and 1.33,respectively. The variation of the ratio reveals more significant effect on the grain size in B-site rich samples than that in A-site rich samples. The dissipation factor decreases rapidly from 0.1 to 0.01 at 1 MHz with decreasing (Ba+Sr)/Ti ratio. The tunability increases with decreasing ratio from 1.33 to 1.05,and then decreases with decreasing ratio from 1.05 to 0.76. The film with (Ba+Sr)/Ti ratio of 1.05 has a maximum tunability of 32% and a dissipation factor of 0.03 at 1 MHz.
其他文献
TiB2P/Al composite was successfully fabricated by squeeze casting technology. Its mechanical and tribological properties were evaluated. The elimination of Ti-A
The single-crystalline nickel nanorods with narrow size distribution and better magnetic properties were synthesized by thermal decomposition of nickel hydroxid
A new anodizing process,which does not contain chromate but can improve the corrosion resistance of magnesium alloys significantly,was developed using a microar
The effect of cobalt on chemical segregation and solution process in three nickel base single crystal superalloys was investigated. Three alloys containing the
The microstructure and superconducting properties of Bi-2223 superconductor fabricated in high magnetic fields were investigated. The results shows that the Bi-
Experiment on seamless tubes of aluminum alloy A6063 with initial thickness deviation of 0-20% was conducted through a free hydraulic bulging with tube ends fre
The stress corrosion sensitivity of 7A52 aluminum alloy was investigated in the artificial sea water through slow stain rate test(SSRT). The stress corrosion cr
Currently requirements of thin-walled tube with small bending radius cause the defects such as wrinkling,overthinning and cross-section distortion more prone to
Aqueous sols and gels of tungstic acid were prepared from Na2WO4 with protonated cation-exchange resin. Nano-tungsten oxide of a microporous lamella was synthes
Because the mechanical performances of 5182 belts used for carbonated drinks cover decrease after baking, the effects of trace addition of V and depression amou