【摘 要】
：
简要介绍了张力退火矫直的基本原理、设备及对AgCu/QSn复合带进行张力退火矫直的试验结果。退火试验温度为200,250,,300,350℃,分别加100,150,200,250MPa张力,氩气保护,退火
【机 构】
：
西北有色金属研究院,西北有色金属研究院,西北有色金属研究院 宝鸡 721014,宝鸡 721014,宝鸡 721014
论文部分内容阅读
简要介绍了张力退火矫直的基本原理、设备及对AgCu/QSn复合带进行张力退火矫直的试验结果。退火试验温度为200,250,,300,350℃,分别加100,150,200,250MPa张力,氩气保护,退火时间分别为1,3min,结果表明,在200～350℃,加张力100～200MPa,退火1min的工艺条件能使复合带AgCu面硬度Hv>1100MPa,QSn面硬度Hv>2000MPa,抗拉强度σ_b>600MPa,延伸率δ>20%,平直度h<2mm。
The basic principle and equipment of tension annealing and the test results of tension annealing and straightening of AgCu / QSn composite strip are briefly introduced. The annealing temperature was 200, 250, 300 and 350 ℃, and the tension was 100, 150, 200 and 250 MPa respectively. The time of argon protection and annealing were respectively 1,3 min. The results showed that the process conditions of 200 ~ 350 ℃, The hardness of the composite strip with AgCu surface is Hv> 1100MPa, the QSn surface hardness is Hv> 2000MPa, the tensile strength is σ_b> 600MPa, the elongation is δ> 20% and the flatness is h <2mm.
其他文献
采用两层多晶硅表面微加工工艺,研制开发了一种新型的微型可编程闪耀光栅.该光栅具有结构简单、工作谱段宽、光谱连续可调等特点.为了实现可工作闪耀角的最大化,有效利用Dimp
通过采用转移矩阵方法求解自旋电子隧穿过程,理论研究了半导体超晶格系统中电子自旋输运的磁电调控行为.结果表明:仅对超晶格系统施以磁调制,隧穿系数将出现自旋分裂,随磁场
10月9日至13日,全国会计领军(后备)人才第四次联合集中培训在北京国家会计学院开班。10月8日晚,中注协召集注册会计师类学员召开了集中培
From October 9 to October 13, th
我国经济体制发生了哪些变化？安徽临泉县读者沈金生来信问：经过１５年改革，我国的经济体制发生了哪些变化？沈金生同志：经过１５年改革，我国经济体制已进入一个新的历史阶段，改革侧重点从突破
5月10日,交通运输部部长李盛霖与水利部部长陈雷就加强两部合作、促进水运和水利发展进行会谈,并在会谈后签署合作备忘录。合作备忘录明确提出:一是加强规划协调。两部在有关
俄罗斯的市场经济改革已历经五年有余。从总体上看,在推行休克疗法的几个前苏东国家中,俄罗斯属于效果不太明显的几个国家之一,其经济从1990年开始出现负增长,以后又连续四
井式回火炉是热处理生产中常用的设备,其炉盖上的风机轴设计时选用Cr18型不锈钢制造,材料昂贵,机加工麻烦,市场销售最低价格为480元/根。 我厂的中温(400℃)井式回火炉风机
当今世界经济发展格局中,有一个极具活力的地区:它是怎样发展的?又有哪些做法可供参考? 本世纪70年代,当发达国家由于石油危机而放慢经济发展速度,年平均经济增长率停留在2％
氧燃气火焰切割连铸板坯是连铸生产中一种已定形的工艺。然而,这种传统的火焰切割技术的缺点是切割速度比较低。为提高切割速度,奥地利和德国联合开发出Loxjet工艺。该工艺
天保工程实施10年来在调减木材产量、分流安置富余职工、安排政社性资金补助、实行目标责任考核等方面,为森工企业改革减轻了内部压力和提供了外部动力。文章列举并分析了较