对AZ31B镁合金半固态挤压成形管材进行了试验研究,确定了材料加热温度、搅拌时间、搅拌速率、静置时间及半固态浆料浇注温度等成形工艺参数,分析了镁合金管材挤压制件的显微
论文部分内容阅读
对AZ31B镁合金半固态挤压成形管材进行了试验研究,确定了材料加热温度、搅拌时间、搅拌速率、静置时间及半固态浆料浇注温度等成形工艺参数,分析了镁合金管材挤压制件的显微组织与力学性能及其影响因素。结果表明,半固态镁合金挤压制件组织的晶粒细化,小而均匀,尖角钝化,表现出明显的塑性变形特征;制件的抗拉强度、伸长率、断面收缩率、硬度及冲击韧度均有较大幅度的提高。
The semi-solid extruded AZ31B magnesium alloy pipe was studied, and the forming process parameters such as heating temperature, stirring time, stirring rate, standing time and semi-solid slurry pouring temperature were determined. Microstructure and Mechanical Properties of Part and Influencing Factors. The results show that the grain refinement of the semi-solid magnesium alloy extruded parts is small, uniform and sharp, and shows obvious plastic deformation characteristics. The tensile strength, elongation, reduction of area, Hardness and impact toughness have a more substantial increase.
其他文献
采用一种新型形变热处理方法在工业条件下制备了1420铝锂合金超塑性板材,通过高温拉伸、金相、扫描电镜观察等检测分析手段研究了该板材的超塑性能。组织观察表明,该板材具有
钛合金的晶粒尺寸对其超塑性能有着显著影响。采用三维镦拔形变热处理工艺对供货态的TC4合金进行细晶化处理,然后采用恒应变速率法对细晶TC4合金的超塑性进行了研究。结果表
介绍近十几年来薄壳的建模与控制研究所取得的一系列重要进展.主要内容包括对具有任意形状中面以及不同物理背景的3种经典薄壳——浅壳、Naghdi壳和Koiter壳的坐标卡无关的数
半固态成形技术是一种金属成形的新方法,它具有铸锻工艺的综合优点。利用应变诱导熔化激活法(SIMA法)制备了7A09铝合金半固态坯料,研究了预变形量对7A09铝合金半固态组织的影
简述了干式缸套气缸体水套砂芯四开盒热芯盒在生产实践中较为普遍存在的两种不同结构设计方案;对其盒体的结构特点、左右盒体的承载方式、芯盒本体的结构大小、盒体的制作难
根据实例探讨了Cr残余高时引起的熔炼不良而造成铸件气孔缺陷的原因,并提出了相关预防措施。
According to the example, the cause of the defects caused by poor smeltin
对柴油机机身铸件进行CAD/CAE技术研究,并应用CAE软件ProCAST建立起仿真验证与实际验证相结合的铸造工艺仿真验证平台。实践证明,该铸造工艺仿真验证平台可为现场生产提供技
在热力学计算的基础上,分析了20CrMo含硫齿轮钢钙处理的工艺条件,并对钙处理后的含硫齿轮钢轧材进行了取样研究。结果表明,钙处理前钢中氧含量(wO)控制在10×10-6以下,可使加
通过数学方法建立砂芯传热模型再现了砂芯在整个浇注过程中内部发生的各种变化,研究了铝合金铸件生产过程中浇注温度和溃散剂对酚醛树脂覆膜砂溃散性的影响。结果表明,提高浇
QT500-10轮毂铸件常用于重型卡车。为了保证铸件具有较高的抗拉强度和较好的伸长率,并且同时提高生产效率、降低成本,在试制过程中对铸件的成分、浇注系统和泥芯结构设计等方