This paper reports that the transverse laser induced thermoelectric voltages (LITV) are observed for the first time in the step flow growth (1-x)Pb(Mg1/3Nb2/3)O3-xPbTiO3 (PMN-PT,x = 0.20, 0.33, 0.50) thin films deposited on vicinal-cut strontium titanate single crystal substrates. Because lead magnesium niobate-lead titanate is a solid solution of lead magnesium niobate (PMN) and lead titanate (PT), there are two types of signals. One is wide with a time response of a microsecond, and the other superimposed with the wide signal is narrow with a time response of a nanosecond. The transverse LITV signals depend on the ratio of PMN to PT drastically. Under the irradiation of 28-ns pulsed KrF excimer laser with the 248-nm wavelength,the largest induced voltage is observed in the 0.50Pb(Mg1/Nb2/3)O3-0.50PbTiO3 films. Moreover, the effects of film thickness, substrates, and tilt angles of substrates are also investigated.
This paper reports that the transverse laser induced thermoelectric voltages (LITV) are observed for the first time in the step flow growth (1-x) Pb (Mg1 / 3Nb2 / 3) O3-xPbTiO3 (PMN- , 0.50) thin films deposited on vicinal-cut strontium titanate single crystal substrates. Because lead magnesium niobate-lead titanate is a solid solution of lead magnesium niobate (PMN) and lead titanate (PT), there are two types of signals. One is wide with a time response of a microsecond, and the other superimposed with the wide signal is narrow with a time response of a nanosecond. The transverse LITV signals depend on the ratio of PMN to PT drastically. Under the irradiation of 28-ns pulsed KrF excimer laser with the 248-nm wavelength, the maximum induced voltage is observed in the 0.50Pb (Mg1 / Nb2 / 3) O3-0.50PbTiO3 films. Moreover, the effects of film thickness, substrates, and tilt angles of the substrates are also investigated .