A new steel matrix wear resistant composite reinforced by in situ granular eutectics can be obtained by modifying with a Si-Ce-Ti compound in the steel melt. The result indicates that the in situ granular eutectic is a pseudo-eutectic of austenite and (Fe,Mn)3C, which is formed between austenite dendrites during solidification due to the segregation of C and Mn impelled by modifying elements. The quantity of in situ granular eutectic reaches up to 8%-12% and its grain size is in the range from 10um to 20um. The austenite steel matrix wear resistant composite reinforced by in situ granular eutectic (abbreviated AGE composite) and austenite-bainite steel mains wear resistant composite reinforced by in situ granular eutectic (abbreviated ABGE composite) are obtained in the as-cast state and by air hardening, respectively. The wear resistance of the AGE and ABGE composites can be more greatly increased than that of their matrix steels under low and medium impact working condition. A new steel matrix resistant resistant composite reinforced by in situ granular eutectics can be obtained by modifying with a Si-Ce-Ti compound in the steel melt. The result indicates that the in situ granular eutectic is a pseudo-eutectic of austenite and (Fe , Mn) 3C, which is formed between austenite dendrites during solidification due to the segregation of C and Mn impelled by modifying elements. The quantity of in situ granular eutectic reaches up to 8% -12% and its grain size is in the range from 10um to 20um. The austenite steel matrix wear resistant composite reinforced by in situ granular eutectic (abbreviated AGE composite) and austenite-bainite steel mains wear resistant composite reinforced by in situ granular eutectic (abbreviated ABGE composite) are obtained in the as-cast state and by air hardening, respectively. The wear resistance of the AGE and ABGE composites can be more greatly increased than that of their matrix steels under low and medium impact working conditions.