【摘 要】
：
以CuCl2·2H2O为铜源,InCl3·4H2O为铟源,L-半胱氨酸为硫源,N,N二甲基甲酰胺(N,N-dimethylformamide,DMF)为溶剂,在180℃下反应16h合成了CuInS2微晶。用X射线粉末衍射仪、X射
论文部分内容阅读
以CuCl2·2H2O为铜源,InCl3·4H2O为铟源,L-半胱氨酸为硫源,N,N二甲基甲酰胺(N,N-dimethylformamide,DMF)为溶剂,在180℃下反应16h合成了CuInS2微晶。用X射线粉末衍射仪、X射线光电子能谱、场发射扫描电子显微镜对产物的结构、形貌、相组分进行表征。结果表明产物是由厚度为10～50nm纳米片组成的球状CuInS2微晶。并对由纳米片组成的球状CuInS2微晶的形成机理进行了简单探讨。
CuCl2 · 2H2O was used as the copper source, InCl3 · 4H2O as the indium source, L-cysteine as the sulfur source and N, N-dimethylformamide (DMF) as the solvent to react at 180 ℃ 16h synthesized CuInS2 crystallites. The structure, morphology and phase composition of the product were characterized by X-ray powder diffraction, X-ray photoelectron spectroscopy and field emission scanning electron microscopy. The results show that the product is a spherical CuInS2 crystallite composed of 10-50 nm nanosheets. The formation mechanism of spherical CuInS2 microcrystals composed of nanosheets was briefly discussed.
其他文献
研究了恒变幅疲劳载荷作用下Al-Si-Mg合金的疲劳行为及微结构对其疲劳性能的影响.对恒变疲劳载荷作用下Al-Si-Mg合金的单轴疲劳寿命以及疲劳行为进行了研究.利用透射透射电子
随着金融市场的深化改革和我国社会主义市场经济的进一步改革推进,作为金融系统的重要部分,银行业面对着越来越大竞争压力,为此,加快我国商业银行经营转型升级,推进我国商业
以NaYF_4为代表的上转换纳米晶作为细胞及组织标记的研究越来越热。但易团聚,水溶性、生物兼容性差,没有与生物偶联官能团等缺点限制了其应用,因而表面修饰显得尤为重要。作
采用磁控溅射方法,在不同功率下合成Sn-Ni-Al三元合金负极材料,通过SEM对表面形貌进行表征,并装成CR2016型扣式电池进行充放电及循环伏安测试.结果表明,颗粒溅射时以线性生长
提出一种利用超声波声压反射系数相位谱无损测量热障涂层密度的新方法。采用电子束物理气相沉积技术(electric beam physical vapor deposit,EBPVD)制备平均厚度为150μm的Zr
人的精力是有限的,不应把一生的重点放在不断改进自己的缺点上,只想把自己培养成“完人”;而应经常分析发现自己的优点,并将它持续不断地发扬光大,形成自己独特的优势,成为某
引入元素Nb对SO42-/ZrO2进行改进,制备了SO42-促进的Zr-Nb新型二元氧化物固体超强酸催化剂SO42-/ZrO2-Nb2O5.以合成乙酸正丁酯为探针反应,考察了该催化剂的制备工艺,确定了最
在Pt电极上,利用正交优化法于353 K的乙酰胺-尿素-NaBr-KBr熔体中电沉积制备了性能各异的二元铁族金属合金膜,即Fe-Co、Fe-Ni及Co-Ni,分析获得最佳性能的磁性膜及其工艺参数;
为研究自蔓延和热爆两种燃烧合成方式对产物Ni3Al组织的影响,采用扫描电子显微镜(SEM)观察对比了合成试样中的不同显微组织,利用X射线衍射(XRD)分析比较了合成产物相的差别,
基于球形压入的工作方式,重点研究金属材料塑性参数的表征方法.首先,选取压入总功和Meyer系数作为主要分析参数.其次,利用孔洞模型、相似解和数值模拟等工具,分别建立压入总