Hypoeutectic Fe-Cr-B-C hardfacing alloys with different molybdenum( Mo) contents( The design content was 0,2,3. 3 and 4. 5 wt. %,respectively) were deposited using the flux-cored wire by means of metal active gas arc welding. The effects of Mo on the refi