The aluminum matrix composites (AlB2+α-Al2O3)/Al were fabricated by in situ reaction synthesis from an Al-B2O3 system. The reaction pathways, apparent activation energies and tensile properties were analyzed by using differential scanning calorimetry (DSC
【机 构】
：
Shanghai Aircraft Design and Research Institute, Shanghai 201210, China;School of Materials Science
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
The aluminum matrix composites (AlB2+α-Al2O3)/Al were fabricated by in situ reaction synthesis from an Al-B2O3 system. The reaction pathways, apparent activation energies and tensile properties were analyzed by using differential scanning calorimetry (DSC), X-ray diffraction (XRD), scanning electron microscopy (SEM), and equipped energy dispersive spectroscopy (EDS). The results showed that there are two-step reactions in the Al-B2O3 system. The first-step is 15Al+7B2O3→7α-Al2O3+AlB12+2B and the second-step is 2B+AlB12+6Al→7AlB2. Their corresponding apparent activation energies are 352 and 444 kJ/mol, respectively. The tensile strength and elongation rate of the composites are 190.5 MPa and 6.6％, respectively.Compared with ordinary aluminum base material, the performance is superior. There are many dimple and cracked α-Al2O3 reinforcements in tensile fracture surface layer.
其他文献
Nitrogen and sulfur co-doped porous nanocarbon (ZIF-C-N-S) catalyst was successfully synthesized derived from ZIF-8 and thiourea precursors. The electrochemical measurements indicate that the as-obtained ZIF-C-N-S catalyst exhibits higher electrocatalytic
A novel aqueous Sn-S complex solution was applied as precursor to fabricate SnO2 electron selective layers (ESLs) for the hybrid perovskite solar cells (PSCs). The tin and sulfur powder were directly dissolved in a (NH4)2S water solution to form Sn-S prec
Three different kinds of sepiolite (Type A, Type B and Sepiolite fiber) were processed by calcination and analyzed by thermogravimetric analysis (TG), X-ray diffraction diffractometer (XRD), scanning electron microscopy (SEM), BET (specific surface area f
Herein, two nanoparticles with different dimensions, spherical carbon dots (C-dots) and sheet-like hectorite clay, were used as physical crosslinkers to fabricate C-dots-clay-poly(N-isopropylacrylamide) nanocomposite hydrogels (coded as C-dots-clay-PNIPAm
To evaluate the property and degradation characteristics of concrete prepared with aggregate contained montmorillonite,concretes were prepared with aggregates contained montmorillonite,and then concrete slump loss,compressive strength,electric flux,the re
2198 and 5A90 Al-Li alloys were anodized with a constant DC potential in 18％H2SO4 solution (Solu.A) and the mixture solution of 18％H2SO4+5％C2H2O4 (Solu.B) at room temperature.12 and 11 V was optimized as the applied oxidation potential for 2198 and 5A90 a
A niobate/titanat nanoflakes (Nb/TiNFs) composite was synthesized via the hydrothermal method and used to remove Pb(II) from water. XRD, TEM, and SEM results indicate that Nb/TiNFs appear as nanoflakes, of which the primary crystal phase is tri-titanate.
The modification of graphitic carbon nitride can significantly improve the photocatalytic performance of graphitic carbon nitride (g-C3N4). Fe2O3/nitrogen-deficient g-C3N4-x composite catalysts were prepared with dicyandiamide as the precursor and Fe3+ do
Based on the experimental analysis and theoretical calculation,the self-propagating high temperature synthesis of TiB2/Fe composite was studied.The experimental results show that the interfacial between TiB2 and Fe was smooth and clear,and the composite b
SiC/7075 aluminum matrix composites were prepared by a liquid stirring method. The role of Ti facilitating the preparation of SiC/7075 aluminum matrix were studied by means of direct-reading spectrometer, scanning electron microscope, energy dispersive sp