对用含硫2~4%(重量)的油焦制成的阳极糊进行了研究。焦碳在实验室条件下,在1250℃煅烧三小时,干料的粒度组成与克拉斯诺雅尔斯克铝厂所用的相类似,在所有试料中粘结剂的含量均为31%(重量)。用实验室装置分析焦化气体。将50克阳极
Anode pastes made with 2 to 4% by weight of oil coke were studied. The coke was calcined at 1250 ° C for three hours under laboratory conditions. The dry material had a particle size composition similar to that used by the Krasnoyarsk Aluminum Works, with a binder content of 31% by weight (weight ). Coking gas is analyzed using laboratory equipment. 50 grams of anode