Oxidation behaviors of TP304H steel with electrophoresis deposited CeO2 coating in water vapor were studied at 610℃~770℃ for 65 h. The results showed that CeO2 coating reduced effectively the oxidation rate of TP304H. Analysis with SEM and EDS showed the structure of oxide scale turned from multi-layer to mono-layer and oxide scale with high Cr content formed on the surface of CeO2 coating while inner oxidation disappeared. Based on test results and CeO2 characters that Ce ion can vary between Ce4+ and Ce3+ under oxygen-rich and oxygen-poor environment, it is concluded that CeO2 coating acts as a barrier to prevent oxygen inner diffusion and the partial oxygen pressure of CeO2 coating-substrate interface is limited. Cr first diffuses outward across CeO2 coating and forms oxide scale on the surface, which delays formation of Fe oxide.
Oxidation behaviors of TP304H steel with electrophoresis deposited CeO2 coating in water vapor were studied at 610-770 ° C for 65 h. The results showed that CeO2 coating reduced effectively the oxidation rate of TP304H. Analysis with SEM and EDS showed the structure of oxide scale based on test results and CeO2 characters that Ce ion can vary between Ce4 + and Ce3 + under oxygen-rich and oxygen -poor environment, it is concluded that CeO2 coating acts as a barrier to prevent oxygen inner diffusion and the partial oxygen pressure of CeO2 coating-substrate interface is limited. Cr first diffuses outward across CeO2 coating and forms oxide scale on the surface, which delays formation of Fe oxide.