【摘 要】
：
A sort of rare earth Mg-based system hydrogen storage alloys with AB3-type was prepared by double-roller rapid quenching method. The alloys were nanocrystalline
【机 构】
：
Research Institute of Rare Metal
论文部分内容阅读
A sort of rare earth Mg-based system hydrogen storage alloys with AB3-type was prepared by double-roller rapid quenching method. The alloys were nanocrystalline multi-phase structures composed of LaNi3 phase and LaNi5 phase by X-ray diffraction and scanning electron microscopy analyses, and the suitable absorption/desorption plateau was revealed by the measurement of P-C-I curve. Electrochemical studies indicate that the alloys exhibit good electrochemical properties such as high capacity and stable cycle life, and the discharge capacity is 369 mAh·g-1 at 0.2 C (72 mA·g-1), after 460 cycles, the capacity decay was only 19.4% at 2 C (720 mA·g-1).
其他文献
Porous silicon nitride ceramics with difference volume fractions of porosity from 34.1% to 59.2% were produced by adding different amount of the pore-forming ag
Equal-channel angular pressing(ECAP) of an enhanced solid-solution treated 2024 Al alloy was successfully performed at room temperature, with an imposed equival
A self-made directional solidification device was used to fabricate d 80 mm high purity aluminum ingots. SEM and AFM were used to detect the shape of grain boun
Thimble zirconia oxygen sensors were prepared with yttria stabilized zirconia(YSZ). The surfaces of the electrode,electrolyte and their interface were observed
Microstructure variation of spray-formed Si-30%Al alloy during densification process by hot pressing was studied. The results indicate that the microstructure o
Friction stir welding (FSW) is a new and promising welding processing that can produce low-cost and high-quality joints of aluminum alloys. 1 mm thick sheets of
Dynamic adaptation of multimedia content is seen as an important feature of next generation networks and pervasive systems enabling terminals and applications t
The effect of the ground granulated blast-furnace slag (GGBFS) addition, the modulus n (mole ratio of SiO2 to Na2 O ) and the concentration of sodium silicate s
The ratio of Fe-Al compound at interCace, which could determine the quantity of Fe-Al compound at the interface of steel-mushy Al-20Sn bonding plate, was used t
C2Cl6 was used as grain refiner for AM60 magnesium alloys. The effects of grain refinement process on chemical composition, microstructure, impact energy, hardn