The two-step hydro-bulge forming technique was proposed to manufacture the ellipsoidal shell with the length ratio of the long axis to the short axis larger than 1.4. A central tube was introduced into the first step of the hydro-bulge forming process to constrain the over growth of the short axis during bulging,and then the central tube was replaced with two polar plates in the second step of the hydro-bulge forming process to manufacture an integral ellipsoidal shell. It is shown that the central tube restricts the growth of the short axis and simultaneously reduces the shrunk tendency of the long axis. The wrinkling occurs due to the latitudinal compressive stress at the equator at the early stage of hydro-bulge forming. However,with the increase of internal pressure,the compressive stress areas gradually decrease and finally the tensile latitudinal stress occupies approximately the whole shell,thus the wrinkles are eliminated. A sound ellipsoidal shell with the axis length ratio of 1.8 is obtained after two-step hydro bulging.
The two-step hydro-bulge forming technique was proposed to manufacture the ellipsoidal shell with the length ratio of the long axis to the short axis larger than 1.4. A central tube was introduced into the first step of the hydro-bulge forming process to constrain the over growth of the short axis during bulging, and then the central tube was replaced with two polar plates in the second step of the hydro-bulge forming process to manufacture an integral ellipsoidal shell. It shows shown the the central tube restricts the growth of the short axis and simultaneously reduces the shrunk tendency of the long axis. The wrinkling occurs due to the latitudinal compressive stress at the equator at the early stage of hydro-bulge forming. However, with the increase of internal pressure, the compressive stress decrease and finally the tensile latitudinal stress occupies approximately the whole shell, thus the wrinkles are eliminated. A sound ellipsoidal shell with the axis length ratio of 1.8 is obtained after two-step hydro bulging.