摘 要：为研究高温后不同冷却方式下混凝土钢筋的粘结滑移性能，对39个高温后混凝土试件进行中心拉拔试验，并完成自然冷却方式下试件的劈裂抗拉强度试验，分析温度和冷却方式对试件峰值粘结应力和峰值滑移的影响，建立了不同冷却方式下峰值粘结应力、峰值滑移与温度的关系式，提出考虑初始温度损伤的粘结滑移全曲线方程，并基于粘结强度理论模型计算了自然冷却方式下的粘结强度理论值。结果表明：随着温度的升高，峰值粘结应力线性下降，500 ℃时粘结强度损失达80.5%，峰值滑移随温度升高呈先减小后增大的趋势，不同冷却方式对峰值粘结应力和峰值滑移的影响不明显;考虑损伤的理论粘结滑移全曲线与试验曲线拟合度较好;采用理论模型计算的粘结强度与试验值较吻合。
关键词：高温;冷却方式;钢筋混凝土;粘结滑移;粘结强度
Abstract： In order to study the concrete-rebar bond-slip performance under different cooling ways after high temperature， a central pull-out test had been carried out on 39 reinforced concrete specimens after high temperature， and the splitting tensile strength test of the specimens under natural cooling had been completed. The effect of high temperature and different cooling ways on peak bond stress and peak slip of the specimens are discussed in this paper. The calculation equations between peak bond stress， peak slip and temperature have been established， and the full curve equation of bond-slip considering initial temperature damage has been proposed. Based on the theoretical model of bond strength， the theoretical value of bond strength under natural cooling has been calculated. The results show that as the temperature increases， the peak bond stress decreases linearly. At 500 ℃， the bond strength loss reached 80.5%， and the peak slip showed a trend of first decreasing and then increasing with growth of temperature. The effect of different cooling ways on peak bond stress and peak slip is not obvious. The theoretical bond-slip full curves considering damage has a good fit with the test curves; The bond strength calculated by the theoretical model is in good agreement with the test value.
Keywords：high temperature; cooling ways; reinforced concrete; bond-slip; bond strength
隨着中国经济的迅速发展，城市高层建筑密度大、易发生重大火灾。钢筋混凝土结构在火灾后会出现不同程度的损伤，从而导致建筑物倒塌，造成经济损失，给社会安全带来巨大威胁。粘结是钢筋混凝土间一种复杂的相互作用，足够的粘结强度是钢筋混凝土发挥良好工作性能的基础，因此，研究钢筋混凝土在火灾后的粘结性能退化十分必要。已有许多学者研究温度对混凝土力学性能[1]和钢筋混凝土粘结性能的影响，Bi等[2]和Karolina等[3]研究发现，温度越高，混凝土的抗压强度越低;杨婷等[4]研究发现，混杂纤维超高性能混凝土在1 000 ℃后保持67%的残余强度;周子健等[5]和Ergün等[6]通过中心拉拔试验发现，高温后钢筋与混凝土的粘结强度随着温度升高呈下降趋势;杨鸥等[7]则发现粘结强度在200 ℃时稍有回升，大于200 ℃后急剧下降。火灾发生后，根据受灾程度不同存在消防射水或消防安全系统自动喷水等不同的冷却方式，目前学者们集中研究冷却方式对混凝土力学性能的影响，贾福萍等[8]、曲海坤等[9]研究发现，250 ℃高温后混凝土自然冷却的强度比喷水冷却的强度大，但当温度升到450 ℃后则相反。考虑到不同冷却方式可能对钢筋混凝土粘结性能存在一定影响，笔者通过中心拉拔试验，研究不同冷却方式对高温后钢筋混凝土粘结滑移性能的影响，为不同冷却方式下高温试件的深入研究提供参考。
1 试验概况
1.1 原材料与配合比
粗骨料购于南宁市武鸣区某石场，其基本物理性能如表1所示;细骨料购于南宁市云桥建材市场，骨料粒径为0.16～4.75 mm，细度模数为2.98，粗细骨料均为连续级配;水泥为海螺牌P.O.42.5普通硅酸盐水泥;拌合水来自实验室自来水;钢筋为精轧螺纹钢筋PSB575，直径20 mm。根据《普通混凝土配合比设计规程》（JGJ 55—2011）中的相关规定，试验配合比及常温下实测混凝土的立方体抗压强度fcu、劈裂抗拉强度ft见表2，表中W为拌合水，C为水泥，S为天然河沙，NA为天然粗骨料。 1.2 试件设计与试验方法
试验考虑不同温度（20、200、300、400、500 ℃）、冷却方式（自然冷却（ZL）、喷水冷却10 min（PL1）、喷水冷却30 min（PL2）），设计13组立方体抗压试件、13组中心拉拔试件（试件尺寸如图1所示）和5组劈裂抗拉试件（自然冷却方式），每组3个，共93个试件。钢筋粘结段为100 mm，非锚固区利用PVC管控制。高温试验采用RX3-45-9工业电阻炉进行，将不同组别的试件分别升温至恒定温度，升温曲线如图2所示，达到目标温度后，恒温6 h，使试件内外温度保持一致[10]。6 h后切断电阻炉电源，打开炉门，将需要喷水冷却的试块取出，其余试块留在炉内，自然冷却至20 ℃再取出。喷水冷却采用消防灭火喷头在5 m范围内对试件进行喷水处理，通过水表控制喷枪的出水量在15 L/s左右，考虑不充分冷却10 min和充分冷却30 min[11]，喷水处理完成后，将试件放置于实验室环境晾干至20 ℃。
试验加载采用电液伺服岩石多功能试验机（TJW-1000），位移控制加载速度为0.2 mm/min，试验机自动采集加载端的荷载和位移，自由端位移由前后两个对称放置的位移计连接DH3821静态采集仪系统采集，加载设备及装置如图3所示。
2 试验结果及特征值分析
2.1 试验结果
在试验温度工况下，高温前后拉拔试件最终破坏形式均发生劈裂破坏，高温变化未引起试件破坏形态的明显差异。高温前，由于试件没有箍筋约束，拉拔过程中钢筋肋对肋前混凝土产生径向挤压，试件被劈裂成2～3块，发生劈裂破坏;高温后，试件仍出现劈裂破坏，但随着温度的增加，裂缝宽度逐渐减小，当温度达到500 ℃时，试件表面仅出现微小裂缝，不同温度下试件的破坏形态如图4所示。图5为高温后不同冷却方式下混凝土立方体抗压强度试验结果，从图中可以看出，随着温度的升高，混凝土立方体抗压强度逐渐降低，不同冷却方式对立方体抗压强度的影响不明显。
不同冷却方式下试件的粘结滑移曲线如图6所示。假设钢筋与混凝土间的粘结强度沿着锚固长度均匀分布，平均粘结应力由公式τ=pπdl求得[12]。式中：τ为平均粘结力，MPa;p为荷载，kN;d为钢筋直径，mm;l为锚固长度，mm。试件命名规则：（A/B/C）温度序号，其中，A为自然冷却方式系列;B为喷水冷却10 min;C为喷水冷却30 min。以试件A200-1为例，表示经历200 ℃高温后自然冷却的1号试块。从图6可知，不同冷却方式试件的粘结滑移曲线与常温下的十分相似，3种冷却方式下的粘结滑移曲线均表现出同一特征：峰值粘结应力随温度升高而降低，温度越高，粘结滑移曲线下降得越平缓，这是因为高温作用使试件产生初始损伤，降低了试件的峰值粘结应力。
2.2 峰值粘结应力与峰值滑移分析
不同冷却方式下温度与峰值粘结应力的关系，如图7所示。由图7可知，同一温度下，不同冷却方式的峰值粘结应力值都很接近，说明不同冷却方式对试件的峰值粘结应力影响不大。随着温度的升高，不同冷却方式试件的峰值粘结应力均呈现明显线性降低的趋势，由图5可知，随着温度的升高，混凝土立方体抗压强度逐渐降低，且下降趋势大致随温度的升高而加剧，而粘结强度随着抗压强度的减小而减小，因此，峰值粘结应力随着温度的升高呈明显降低的趋势，可知高温作用对试件的粘结性能劣化影响显著。以上分析表明，试件的峰值粘结应力与温度关系密切，采用式（1）来描述高温后的峰值粘结应力，其中R2=0.979。
不同冷却方式下温度与峰值滑移的关系如图8所示。从图8可以看出，不同冷却方式对峰值滑移的影响规律不明显，随着温度的升高，试件的峰值滑移大致呈先减小后增大的趋势，在200 ℃时，3种冷却方式的峰值滑移都达到最小值，总体呈抛物线关系。建议采用式（2）来描述经历高温后试件的峰值滑移，其中R2=0.901 84。
3 高温后损伤本构关系
3.1 粘结滑移损伤本构方程
钢筋与混凝土之间的粘结性能通过粘结滑移曲线表达，采用图9曲线上某点的割线模量来表征试件的粘结损伤程度，曲线上任一點的割线模量都可以用损伤变量β=τ/s来描述。假设常温下界面没有损伤时粘结性能参数为β0，高温后界面出现损伤，粘结性能参数为βT，则高温作用后损伤变量DT定义为DT=（β0-βT）/β0βT=（1-DT）β0。
由Lemaiter应变等价性假说[13-14]可知：应力作用在损伤材料上产生的应变与有效应力作用在无损材料上引起的应变等价。因此，高温后混凝土的损伤全曲线关系可用式（3）表示。
高温后混凝土试件在中心拉拔的加载过程中产生二次损伤，其损伤全曲线关系为：ττ=（1-Dτ）·βTs，式中：Dτ为中心拉拔作用引起的损伤变量。则高温后混凝土在中心拉拔作用下的损伤全曲线关系为：ττ=（1-D）β0s，式中：D为混凝土高温后受中心拉拔作用的总损伤变量，D=DT+Dτ-DTDτ。
分段构建损伤模型，受力状态峰值粘结应力前采用Weibull统计分布，峰值后则在过镇海等[15-16]损伤模型的基础上引入曲线形状控制参数a和b来描述峰后曲线的收敛段。总损伤变量D表达式如（4）所示。式中，两个材料强度参数计算式为m=1/ln（βTsu/ττ），ρ=ττ/（βTsu）;a和b可通过拟合得到。高温后混凝土在中心拉拔作用下的粘结滑移损伤全曲线模型如式（5）所示。
利用式（5）对实测曲线进行拟合，不同冷却方式任取一个温度得到如图10所示粘结滑移全曲线，从图10可以看出，计算结果与实测结果的吻合程度较高，拟合度较好，相关参数见表3。
3.2 界面D-s损伤曲线分析
根据式（3）得到中心拉拔试件的损伤滑移曲线（D-s曲线），如图11所示。可以看出，试件的损伤发展过程大致可以分为3个阶段：初始损伤阶段、损伤快速发展阶段、损伤缓慢积累阶段。粘结破坏过程中任意时刻界面损伤发展速度可由曲线上相应点的斜率来反映，斜率越大，损伤发展速度越大。
关键词：高温;冷却方式;钢筋混凝土;粘结滑移;粘结强度
Abstract： In order to study the concrete-rebar bond-slip performance under different cooling ways after high temperature， a central pull-out test had been carried out on 39 reinforced concrete specimens after high temperature， and the splitting tensile strength test of the specimens under natural cooling had been completed. The effect of high temperature and different cooling ways on peak bond stress and peak slip of the specimens are discussed in this paper. The calculation equations between peak bond stress， peak slip and temperature have been established， and the full curve equation of bond-slip considering initial temperature damage has been proposed. Based on the theoretical model of bond strength， the theoretical value of bond strength under natural cooling has been calculated. The results show that as the temperature increases， the peak bond stress decreases linearly. At 500 ℃， the bond strength loss reached 80.5%， and the peak slip showed a trend of first decreasing and then increasing with growth of temperature. The effect of different cooling ways on peak bond stress and peak slip is not obvious. The theoretical bond-slip full curves considering damage has a good fit with the test curves; The bond strength calculated by the theoretical model is in good agreement with the test value.
Keywords：high temperature; cooling ways; reinforced concrete; bond-slip; bond strength
隨着中国经济的迅速发展，城市高层建筑密度大、易发生重大火灾。钢筋混凝土结构在火灾后会出现不同程度的损伤，从而导致建筑物倒塌，造成经济损失，给社会安全带来巨大威胁。粘结是钢筋混凝土间一种复杂的相互作用，足够的粘结强度是钢筋混凝土发挥良好工作性能的基础，因此，研究钢筋混凝土在火灾后的粘结性能退化十分必要。已有许多学者研究温度对混凝土力学性能[1]和钢筋混凝土粘结性能的影响，Bi等[2]和Karolina等[3]研究发现，温度越高，混凝土的抗压强度越低;杨婷等[4]研究发现，混杂纤维超高性能混凝土在1 000 ℃后保持67%的残余强度;周子健等[5]和Ergün等[6]通过中心拉拔试验发现，高温后钢筋与混凝土的粘结强度随着温度升高呈下降趋势;杨鸥等[7]则发现粘结强度在200 ℃时稍有回升，大于200 ℃后急剧下降。火灾发生后，根据受灾程度不同存在消防射水或消防安全系统自动喷水等不同的冷却方式，目前学者们集中研究冷却方式对混凝土力学性能的影响，贾福萍等[8]、曲海坤等[9]研究发现，250 ℃高温后混凝土自然冷却的强度比喷水冷却的强度大，但当温度升到450 ℃后则相反。考虑到不同冷却方式可能对钢筋混凝土粘结性能存在一定影响，笔者通过中心拉拔试验，研究不同冷却方式对高温后钢筋混凝土粘结滑移性能的影响，为不同冷却方式下高温试件的深入研究提供参考。
1 试验概况
1.1 原材料与配合比
粗骨料购于南宁市武鸣区某石场，其基本物理性能如表1所示;细骨料购于南宁市云桥建材市场，骨料粒径为0.16～4.75 mm，细度模数为2.98，粗细骨料均为连续级配;水泥为海螺牌P.O.42.5普通硅酸盐水泥;拌合水来自实验室自来水;钢筋为精轧螺纹钢筋PSB575，直径20 mm。根据《普通混凝土配合比设计规程》（JGJ 55—2011）中的相关规定，试验配合比及常温下实测混凝土的立方体抗压强度fcu、劈裂抗拉强度ft见表2，表中W为拌合水，C为水泥，S为天然河沙，NA为天然粗骨料。 1.2 试件设计与试验方法
试验考虑不同温度（20、200、300、400、500 ℃）、冷却方式（自然冷却（ZL）、喷水冷却10 min（PL1）、喷水冷却30 min（PL2）），设计13组立方体抗压试件、13组中心拉拔试件（试件尺寸如图1所示）和5组劈裂抗拉试件（自然冷却方式），每组3个，共93个试件。钢筋粘结段为100 mm，非锚固区利用PVC管控制。高温试验采用RX3-45-9工业电阻炉进行，将不同组别的试件分别升温至恒定温度，升温曲线如图2所示，达到目标温度后，恒温6 h，使试件内外温度保持一致[10]。6 h后切断电阻炉电源，打开炉门，将需要喷水冷却的试块取出，其余试块留在炉内，自然冷却至20 ℃再取出。喷水冷却采用消防灭火喷头在5 m范围内对试件进行喷水处理，通过水表控制喷枪的出水量在15 L/s左右，考虑不充分冷却10 min和充分冷却30 min[11]，喷水处理完成后，将试件放置于实验室环境晾干至20 ℃。
试验加载采用电液伺服岩石多功能试验机（TJW-1000），位移控制加载速度为0.2 mm/min，试验机自动采集加载端的荷载和位移，自由端位移由前后两个对称放置的位移计连接DH3821静态采集仪系统采集，加载设备及装置如图3所示。
2 试验结果及特征值分析
2.1 试验结果
在试验温度工况下，高温前后拉拔试件最终破坏形式均发生劈裂破坏，高温变化未引起试件破坏形态的明显差异。高温前，由于试件没有箍筋约束，拉拔过程中钢筋肋对肋前混凝土产生径向挤压，试件被劈裂成2～3块，发生劈裂破坏;高温后，试件仍出现劈裂破坏，但随着温度的增加，裂缝宽度逐渐减小，当温度达到500 ℃时，试件表面仅出现微小裂缝，不同温度下试件的破坏形态如图4所示。图5为高温后不同冷却方式下混凝土立方体抗压强度试验结果，从图中可以看出，随着温度的升高，混凝土立方体抗压强度逐渐降低，不同冷却方式对立方体抗压强度的影响不明显。
不同冷却方式下试件的粘结滑移曲线如图6所示。假设钢筋与混凝土间的粘结强度沿着锚固长度均匀分布，平均粘结应力由公式τ=pπdl求得[12]。式中：τ为平均粘结力，MPa;p为荷载，kN;d为钢筋直径，mm;l为锚固长度，mm。试件命名规则：（A/B/C）温度序号，其中，A为自然冷却方式系列;B为喷水冷却10 min;C为喷水冷却30 min。以试件A200-1为例，表示经历200 ℃高温后自然冷却的1号试块。从图6可知，不同冷却方式试件的粘结滑移曲线与常温下的十分相似，3种冷却方式下的粘结滑移曲线均表现出同一特征：峰值粘结应力随温度升高而降低，温度越高，粘结滑移曲线下降得越平缓，这是因为高温作用使试件产生初始损伤，降低了试件的峰值粘结应力。
2.2 峰值粘结应力与峰值滑移分析
不同冷却方式下温度与峰值粘结应力的关系，如图7所示。由图7可知，同一温度下，不同冷却方式的峰值粘结应力值都很接近，说明不同冷却方式对试件的峰值粘结应力影响不大。随着温度的升高，不同冷却方式试件的峰值粘结应力均呈现明显线性降低的趋势，由图5可知，随着温度的升高，混凝土立方体抗压强度逐渐降低，且下降趋势大致随温度的升高而加剧，而粘结强度随着抗压强度的减小而减小，因此，峰值粘结应力随着温度的升高呈明显降低的趋势，可知高温作用对试件的粘结性能劣化影响显著。以上分析表明，试件的峰值粘结应力与温度关系密切，采用式（1）来描述高温后的峰值粘结应力，其中R2=0.979。
不同冷却方式下温度与峰值滑移的关系如图8所示。从图8可以看出，不同冷却方式对峰值滑移的影响规律不明显，随着温度的升高，试件的峰值滑移大致呈先减小后增大的趋势，在200 ℃时，3种冷却方式的峰值滑移都达到最小值，总体呈抛物线关系。建议采用式（2）来描述经历高温后试件的峰值滑移，其中R2=0.901 84。
3 高温后损伤本构关系
3.1 粘结滑移损伤本构方程
钢筋与混凝土之间的粘结性能通过粘结滑移曲线表达，采用图9曲线上某点的割线模量来表征试件的粘结损伤程度，曲线上任一點的割线模量都可以用损伤变量β=τ/s来描述。假设常温下界面没有损伤时粘结性能参数为β0，高温后界面出现损伤，粘结性能参数为βT，则高温作用后损伤变量DT定义为DT=（β0-βT）/β0βT=（1-DT）β0。
由Lemaiter应变等价性假说[13-14]可知：应力作用在损伤材料上产生的应变与有效应力作用在无损材料上引起的应变等价。因此，高温后混凝土的损伤全曲线关系可用式（3）表示。
高温后混凝土试件在中心拉拔的加载过程中产生二次损伤，其损伤全曲线关系为：ττ=（1-Dτ）·βTs，式中：Dτ为中心拉拔作用引起的损伤变量。则高温后混凝土在中心拉拔作用下的损伤全曲线关系为：ττ=（1-D）β0s，式中：D为混凝土高温后受中心拉拔作用的总损伤变量，D=DT+Dτ-DTDτ。
分段构建损伤模型，受力状态峰值粘结应力前采用Weibull统计分布，峰值后则在过镇海等[15-16]损伤模型的基础上引入曲线形状控制参数a和b来描述峰后曲线的收敛段。总损伤变量D表达式如（4）所示。式中，两个材料强度参数计算式为m=1/ln（βTsu/ττ），ρ=ττ/（βTsu）;a和b可通过拟合得到。高温后混凝土在中心拉拔作用下的粘结滑移损伤全曲线模型如式（5）所示。
利用式（5）对实测曲线进行拟合，不同冷却方式任取一个温度得到如图10所示粘结滑移全曲线，从图10可以看出，计算结果与实测结果的吻合程度较高，拟合度较好，相关参数见表3。
3.2 界面D-s损伤曲线分析
根据式（3）得到中心拉拔试件的损伤滑移曲线（D-s曲线），如图11所示。可以看出，试件的损伤发展过程大致可以分为3个阶段：初始损伤阶段、损伤快速发展阶段、损伤缓慢积累阶段。粘结破坏过程中任意时刻界面损伤发展速度可由曲线上相应点的斜率来反映，斜率越大，损伤发展速度越大。