摘 要：针对传统装裱工艺中粘胶剂的缺陷，对传统的装裱材料进行改进，将传统的添加物明矾换成纳米ZnO和NaHCO3，进而分别探讨以上两种添加剂对装裱的影响。结果表明，纳米ZnO+NaHCO3结合传统浆糊在热老化条件下pH值接近中性，且在低温下表现出良好的固化作用。
关键词：装裱书法;纳米ZnO;固色性能;热老化
中图分类号：TQ437 文献标识码：A 文章编号：1001-5922（2021）10-0022-03
Preparation， Performance and Application of Adhesive in Calligraphy Mounting
Liu Yushuai
（Academy of Fine Arts， Xianyang Normal University， Xianyang 712000， China ）
Abstract：Aiming at the defects of the adhesive in the traditional mounting process， the traditional mounting materials are improved， and the traditional additive alum is replaced with nanometer ZnO and NaHCO3 ， and then the influence of the above two additives on mounting is discussed separately. The results show that the pH value of nano-ZnO+NaHCO3 combined with traditional paste is close to neutral under heat aging conditions， and it exhibits a good curing effect at low temperatures.
Key words：mounted calligraphy; nano-zno; fixing performance; thermal aging
浆糊作为中国传统书法装裱技术中的粘胶剂，由面粉加热制成，是装裱过程中不可或缺的材料，因此其质量对装裱效果有着至关重要作用。中国现代装裱工艺中粘胶剂大多由浆糊和明矾所制，但研究表明，采用浆糊和明矾制作的粘胶剂对书法作品进行装裱，会给作品带来一定影响。因此，针对以上问题，对传统装裱工艺中的主要材料（浆糊）进行改良，研究不同添加剂的浆糊对装裱效果产生的影响。而通过本研究，期望得到一种环保的、固色效果好的、可用于紙张文物保护的新型粘胶剂。
1 材料与方法
1.1 材料与设备NaHCO3
宣纸（安徽红星造纸厂）、浆糊（实验室自制）、明矾（天津市科密欧化学试剂开发中心，分析纯）、纳米ZnO粉末（舟山明日纳米科技有限公司，分析纯）、NaHCO3粉末（天津市天力换血试剂有限公司，分析纯）、蒸馏水（实验室自制）、墨汁（河东区春溪文化用品厂，工业级）。
UV灯管（东莞市尔谷光电科技有限公司，260W）、小型坩埚（郑州科瑞（集团）耐火材料有限公司）、耐折度测定仪（长春市月明小型实验机有限责任公司，MIT）、全自动色差仪（北京康光光学仪器有限公司，SC-80C）、pH计（上海仪电科学仪器股份有限公司，PHSJ-4F）
1.2 实验步骤
1.2.1 添加剂浆糊对老化后性能影响实验
将制备完成的普通浆糊、明矾浆糊、纳米ZnO浆糊以及含有NaHCO3粉末的纳米ZnO浆糊涂刷在宣纸上，待其干燥后分为两组，分别为测试组和老化组。将测试组的试验宣纸分为两份：将其中一份剪碎后，放入超声波清洗器振荡1h，而后在3000r/min的转速下离心振荡5min后，测试其pH值;另一份通过斜向裁取宽2cm的纸条来测试其耐折度。将老化组的试验宣纸分为两份：将其中一份在UV灯下20d，而后取出检测样本的色度变化;将另一份放入电热鼓风干燥箱中，使其在120℃的条件下放置10d，而后取出检测其色度变化。
1.2.2 温度对纸张固色性能的影响实验
将宣纸裁剪为边长8.5cm的正方形，并印盖墨水。而后将宣纸样本放置在一开大小的宣纸上，分别喷涂0℃和5℃的蒸馏水，而后用自制浆糊完成装裱工作。利用SC-80C全自动色差仪对背景纸上脱落的墨迹进行色差测试，并将其作为评判标准。
1.3 测试性能表征
1.3.1 老化后的耐折度
由于宣纸具有纤维分明、润墨性好等特点，被广泛用于书写和绘画中，但由于纤维横纵排列明显，造成宣纸的横纵向抗拉能力不平衡，且宣纸为手工制作，厚度不一，导致发生宣纸耐折度测试数据不准确的情况，为此，在对样品测试前，将刷好浆糊的宣纸裁剪为边长8.5cm的正方形，并沿其对角线裁出2cm宽的纸条，因此获得斜向的宣纸样本。在完成测试后，将数据进行统一的统计学处理，并运用裁尾均值的方法计算出耐折度的平均值，从而获得不受极值影响的耐折度值。
1.3.2 老化后的pH值变化
为准确了解到纸质书画文物在老化后的pH值变化情况和涂刷浆糊后的pH值，本试验的样本为涂满添加剂浆糊的宣纸，并以pH值的下降程度作为指标，对老化前后的pH值变化进行判定。
1.3.3 老化后的色差变化
为分析老化对宣纸样品颜色产生的影响，需选用一个色度空间代表色差。根据以往经验，本研究运用了Lab色度空间来比较色差变化。具体计算如下：
Lab模式可量化分析颜色色彩分布，也可通过颜色深浅、明亮和色彩的差异，深度分析颜色的色差性质。 2 结果与分析
2.1 老化后耐折度分析
表1为老化前后4组试验样品的耐折度数据。
从表1中不难看出，相比普通浆糊而言，在老化前，3组具有添加剂的浆糊耐折度更高。普通浆糊的耐折米ZnO的浆糊样品耐折度提高了9左右，添加ZnO+NaHCO3 的浆糊提高了10左右。由于宣纸纤维的不均匀性，试验样品无法均匀吸收含有纳米ZnO和纳米ZnO+NaHCO3 的浆糊，部分区域添加剂含量过多，因此出现极值。
在老化后，明矾浆糊样品耐折度小于普通浆糊，含有纳米ZnO和纳米ZnO+NaHCO3 的浆糊样品耐折度大于普通浆糊，两者差别并不大。综上所述，3种具有添加剂的浆糊能明显提高宣纸的耐折性，但随着老化，耐折性会逐渐减弱，且明矾浆糊在老化后其耐折性低于普通浆糊，故此明矾浆糊并不适用于书画装裱。
2.2 老化后pH值
表2为热老化后pH值的变化数据。从表2中可看出，经光老化后，4组试验样品的pH值皆呈现下降趋势。
从表2中看出，在老化前涂刷了普通浆糊、明矾浆糊及纳米ZnO浆糊的宣纸pH值相差无几，涂刷纳米ZnO+NaHCO3 浆糊的宣纸pH值最接近中性。在热老化的条件下，普通浆糊会使宣纸的酸度增加，明矾浆糊以及纳米ZnO浆糊对于宣纸pH值变化的影响并不大，虽然纳米ZnO+NaHCO3浆糊的pH值会由于温度的变化对NaHCO3的功能产生影响而下降，但仍然为3组中pH值最接近中性的浆糊。因此在考虑仅热老化的情况下，选用纳米ZnO+NaHCO3浆糊进行书画装裱为最佳。
2.3 老化后色度分析
实验采用Lab颜色模型对色度结果进行表征。具体色度变化结果如表3所示。
表3为老化后4组样品的色度变化数据。从表中不难看出，4组样本在经光、热老化后都呈现出颜色变暗、变红、变黄的特征，最为明显的变化为经热老化后4组样本Δb*的值高达200，与其色差值相差无几，从而说明了热老化后的纸张泛黄程度高于光老化后。
同时，对比各项数据，在光老化的条件下，普通浆糊、明矾浆糊以及纳米ZnO浆糊试验样品的ΔL*、Δa*、Δb*值差别不大，且色差值保持在22左右;但纳米ZnO+NaHCO3浆糊试验样品的ΔL*、Δa*、Δb*值明显低于前3项数据，整体色差值也为4项数据的最小值。由此可见，在光老化的条件下，将ZnO+NaHCO3加入浆糊中可以有效的保护纸张颜色。
2.4 低温对跑墨的影响
采用Lab色彩体系，以空白宣纸色度为基准，对空白处和墨迹处的色差值进行检测。表4为普通对照组墨迹Lab色差数据;表5为0℃、5℃蒸馏水喷涂后墨迹的Lab色差平均值对比。
从表4可知，整体数据没有较大差异，因此可说明NaHCO3对脱墨问题不会产生影响。
从表5中看出，低温处理后的样本色差值小于对照组样品。其中ΔE对照组与ΔE5℃仅相差0.88，从肉眼观看几乎看不出明显的色度差异，但与ΔE0℃相差35.21，色差值大，可用肉眼明显观察到色度差别。综上可知，在进行装裱工作前对宣纸上墨迹进行低温处理可有效提升墨迹的固色性。
4 结论
综上，本研究通过研究在传统浆糊中添加不同添加剂，进而制备新型的装裱用粘胶剂，得到以下2点结论：
（1）在老化试验中，含有明矾、纳米ZnO及纳米ZnO+NaHCO3的浆糊相较于普通浆糊，耐折性获得了提升，但随着光老化，其耐折性会逐步减弱，且由于明矾浆糊在老化后其耐折性低于普通浆糊，因此明矾浆糊并不适用书法装裱;热老化后4种浆糊的pH都有下降，但涂刷了纳米ZnO+NaHCO3浆糊的宣纸的pH值最接近中性，因此在熱老化条件下，选用纳米ZnO+NaHCO3浆糊完成书法装裱为最佳;在光老化的条件下，选用纳米ZnO+NaHCO3浆糊进行书法装裱能够有效的保护纸张颜色，可使其泛黄的速度放缓。由此可见，选用纳米ZnO+NaHCO3添加至浆糊中为最佳。
（2）在确定使用纳米ZnO+NaHCO3浆糊进行书法装裱后，为将装裱过程中对书法作品颜色的影响降到最低，对颜料进行了低温处理。试验结果表明，在装裱前运用0℃蒸馏水对墨迹进行低温处理具有固色作用，且较于传统装裱方法更温和、不会产生有害物质，也不会对整个装裱工作产生影响，故此其可运用与文物保护工作中。
综上所述，运用添加了纳米ZnO+NaHCO3的浆糊完成书法作品的装裱工作，可使作品的保存时间更长、更为完好。
参考文献
[1]殷再生.中国书画装裱工艺探析[J].艺术评鉴，2019（02）：36-38.
[2]贾永超.新时代书画装裱艺术的传承与创新研究[J].池州学院学报，2019，33（02）：110-112.
[3]顾春华.中国古书画装裱丝绸纹样仙鹤纹研究[J].武汉纺织大学学报，2019，32（03）：13-17.
[4]李玉霞.论传统书画装裱工艺的演变[J].河南科技学院学报，2016，36（11）：90-92.
[5]欧秀花，安兴龙，沈佳佳，等.蜂蜡在档案修裱浆糊中的应用研究[J].档案管理，2016（05）：37-39.
[6]欧秀花.添加中药对古籍修裱浆糊性能影响的初步研究[J].图书馆杂志，2017，36（09）：52-59.
[7]陈觉声，刘淑贞，刘雄.微波辅助制备醋酸纳米豆渣纤维素工艺研究[J].中国粮油学报，2014，29（07）：96-101.
[8]赵依洋，姜忠丽，代岚，等.糙米酵素糖化液制备工艺优化研究[J].农业科技与装备，2019（05）：35-37.
[9]王国强.中国古籍修复技术体系构建的原则、思路和框架[J].图书馆论坛，2019，39（10）：134-141.
[10]于川.档案与文物修复对比研究——以纸质档案与古籍为例[J].华东纸业，2020，50（02）：1-7.
关键词：装裱书法;纳米ZnO;固色性能;热老化
中图分类号：TQ437 文献标识码：A 文章编号：1001-5922（2021）10-0022-03
Preparation， Performance and Application of Adhesive in Calligraphy Mounting
Liu Yushuai
（Academy of Fine Arts， Xianyang Normal University， Xianyang 712000， China ）
Abstract：Aiming at the defects of the adhesive in the traditional mounting process， the traditional mounting materials are improved， and the traditional additive alum is replaced with nanometer ZnO and NaHCO3 ， and then the influence of the above two additives on mounting is discussed separately. The results show that the pH value of nano-ZnO+NaHCO3 combined with traditional paste is close to neutral under heat aging conditions， and it exhibits a good curing effect at low temperatures.
Key words：mounted calligraphy; nano-zno; fixing performance; thermal aging
浆糊作为中国传统书法装裱技术中的粘胶剂，由面粉加热制成，是装裱过程中不可或缺的材料，因此其质量对装裱效果有着至关重要作用。中国现代装裱工艺中粘胶剂大多由浆糊和明矾所制，但研究表明，采用浆糊和明矾制作的粘胶剂对书法作品进行装裱，会给作品带来一定影响。因此，针对以上问题，对传统装裱工艺中的主要材料（浆糊）进行改良，研究不同添加剂的浆糊对装裱效果产生的影响。而通过本研究，期望得到一种环保的、固色效果好的、可用于紙张文物保护的新型粘胶剂。
1 材料与方法
1.1 材料与设备NaHCO3
宣纸（安徽红星造纸厂）、浆糊（实验室自制）、明矾（天津市科密欧化学试剂开发中心，分析纯）、纳米ZnO粉末（舟山明日纳米科技有限公司，分析纯）、NaHCO3粉末（天津市天力换血试剂有限公司，分析纯）、蒸馏水（实验室自制）、墨汁（河东区春溪文化用品厂，工业级）。
UV灯管（东莞市尔谷光电科技有限公司，260W）、小型坩埚（郑州科瑞（集团）耐火材料有限公司）、耐折度测定仪（长春市月明小型实验机有限责任公司，MIT）、全自动色差仪（北京康光光学仪器有限公司，SC-80C）、pH计（上海仪电科学仪器股份有限公司，PHSJ-4F）
1.2 实验步骤
1.2.1 添加剂浆糊对老化后性能影响实验
将制备完成的普通浆糊、明矾浆糊、纳米ZnO浆糊以及含有NaHCO3粉末的纳米ZnO浆糊涂刷在宣纸上，待其干燥后分为两组，分别为测试组和老化组。将测试组的试验宣纸分为两份：将其中一份剪碎后，放入超声波清洗器振荡1h，而后在3000r/min的转速下离心振荡5min后，测试其pH值;另一份通过斜向裁取宽2cm的纸条来测试其耐折度。将老化组的试验宣纸分为两份：将其中一份在UV灯下20d，而后取出检测样本的色度变化;将另一份放入电热鼓风干燥箱中，使其在120℃的条件下放置10d，而后取出检测其色度变化。
1.2.2 温度对纸张固色性能的影响实验
将宣纸裁剪为边长8.5cm的正方形，并印盖墨水。而后将宣纸样本放置在一开大小的宣纸上，分别喷涂0℃和5℃的蒸馏水，而后用自制浆糊完成装裱工作。利用SC-80C全自动色差仪对背景纸上脱落的墨迹进行色差测试，并将其作为评判标准。
1.3 测试性能表征
1.3.1 老化后的耐折度
由于宣纸具有纤维分明、润墨性好等特点，被广泛用于书写和绘画中，但由于纤维横纵排列明显，造成宣纸的横纵向抗拉能力不平衡，且宣纸为手工制作，厚度不一，导致发生宣纸耐折度测试数据不准确的情况，为此，在对样品测试前，将刷好浆糊的宣纸裁剪为边长8.5cm的正方形，并沿其对角线裁出2cm宽的纸条，因此获得斜向的宣纸样本。在完成测试后，将数据进行统一的统计学处理，并运用裁尾均值的方法计算出耐折度的平均值，从而获得不受极值影响的耐折度值。
1.3.2 老化后的pH值变化
为准确了解到纸质书画文物在老化后的pH值变化情况和涂刷浆糊后的pH值，本试验的样本为涂满添加剂浆糊的宣纸，并以pH值的下降程度作为指标，对老化前后的pH值变化进行判定。
1.3.3 老化后的色差变化
为分析老化对宣纸样品颜色产生的影响，需选用一个色度空间代表色差。根据以往经验，本研究运用了Lab色度空间来比较色差变化。具体计算如下：
Lab模式可量化分析颜色色彩分布，也可通过颜色深浅、明亮和色彩的差异，深度分析颜色的色差性质。 2 结果与分析
2.1 老化后耐折度分析
表1为老化前后4组试验样品的耐折度数据。
从表1中不难看出，相比普通浆糊而言，在老化前，3组具有添加剂的浆糊耐折度更高。普通浆糊的耐折米ZnO的浆糊样品耐折度提高了9左右，添加ZnO+NaHCO3 的浆糊提高了10左右。由于宣纸纤维的不均匀性，试验样品无法均匀吸收含有纳米ZnO和纳米ZnO+NaHCO3 的浆糊，部分区域添加剂含量过多，因此出现极值。
在老化后，明矾浆糊样品耐折度小于普通浆糊，含有纳米ZnO和纳米ZnO+NaHCO3 的浆糊样品耐折度大于普通浆糊，两者差别并不大。综上所述，3种具有添加剂的浆糊能明显提高宣纸的耐折性，但随着老化，耐折性会逐渐减弱，且明矾浆糊在老化后其耐折性低于普通浆糊，故此明矾浆糊并不适用于书画装裱。
2.2 老化后pH值
表2为热老化后pH值的变化数据。从表2中可看出，经光老化后，4组试验样品的pH值皆呈现下降趋势。
从表2中看出，在老化前涂刷了普通浆糊、明矾浆糊及纳米ZnO浆糊的宣纸pH值相差无几，涂刷纳米ZnO+NaHCO3 浆糊的宣纸pH值最接近中性。在热老化的条件下，普通浆糊会使宣纸的酸度增加，明矾浆糊以及纳米ZnO浆糊对于宣纸pH值变化的影响并不大，虽然纳米ZnO+NaHCO3浆糊的pH值会由于温度的变化对NaHCO3的功能产生影响而下降，但仍然为3组中pH值最接近中性的浆糊。因此在考虑仅热老化的情况下，选用纳米ZnO+NaHCO3浆糊进行书画装裱为最佳。
2.3 老化后色度分析
实验采用Lab颜色模型对色度结果进行表征。具体色度变化结果如表3所示。
表3为老化后4组样品的色度变化数据。从表中不难看出，4组样本在经光、热老化后都呈现出颜色变暗、变红、变黄的特征，最为明显的变化为经热老化后4组样本Δb*的值高达200，与其色差值相差无几，从而说明了热老化后的纸张泛黄程度高于光老化后。
同时，对比各项数据，在光老化的条件下，普通浆糊、明矾浆糊以及纳米ZnO浆糊试验样品的ΔL*、Δa*、Δb*值差别不大，且色差值保持在22左右;但纳米ZnO+NaHCO3浆糊试验样品的ΔL*、Δa*、Δb*值明显低于前3项数据，整体色差值也为4项数据的最小值。由此可见，在光老化的条件下，将ZnO+NaHCO3加入浆糊中可以有效的保护纸张颜色。
2.4 低温对跑墨的影响
采用Lab色彩体系，以空白宣纸色度为基准，对空白处和墨迹处的色差值进行检测。表4为普通对照组墨迹Lab色差数据;表5为0℃、5℃蒸馏水喷涂后墨迹的Lab色差平均值对比。
从表4可知，整体数据没有较大差异，因此可说明NaHCO3对脱墨问题不会产生影响。
从表5中看出，低温处理后的样本色差值小于对照组样品。其中ΔE对照组与ΔE5℃仅相差0.88，从肉眼观看几乎看不出明显的色度差异，但与ΔE0℃相差35.21，色差值大，可用肉眼明显观察到色度差别。综上可知，在进行装裱工作前对宣纸上墨迹进行低温处理可有效提升墨迹的固色性。
4 结论
综上，本研究通过研究在传统浆糊中添加不同添加剂，进而制备新型的装裱用粘胶剂，得到以下2点结论：
（1）在老化试验中，含有明矾、纳米ZnO及纳米ZnO+NaHCO3的浆糊相较于普通浆糊，耐折性获得了提升，但随着光老化，其耐折性会逐步减弱，且由于明矾浆糊在老化后其耐折性低于普通浆糊，因此明矾浆糊并不适用书法装裱;热老化后4种浆糊的pH都有下降，但涂刷了纳米ZnO+NaHCO3浆糊的宣纸的pH值最接近中性，因此在熱老化条件下，选用纳米ZnO+NaHCO3浆糊完成书法装裱为最佳;在光老化的条件下，选用纳米ZnO+NaHCO3浆糊进行书法装裱能够有效的保护纸张颜色，可使其泛黄的速度放缓。由此可见，选用纳米ZnO+NaHCO3添加至浆糊中为最佳。
（2）在确定使用纳米ZnO+NaHCO3浆糊进行书法装裱后，为将装裱过程中对书法作品颜色的影响降到最低，对颜料进行了低温处理。试验结果表明，在装裱前运用0℃蒸馏水对墨迹进行低温处理具有固色作用，且较于传统装裱方法更温和、不会产生有害物质，也不会对整个装裱工作产生影响，故此其可运用与文物保护工作中。
综上所述，运用添加了纳米ZnO+NaHCO3的浆糊完成书法作品的装裱工作，可使作品的保存时间更长、更为完好。
参考文献
[1]殷再生.中国书画装裱工艺探析[J].艺术评鉴，2019（02）：36-38.
[2]贾永超.新时代书画装裱艺术的传承与创新研究[J].池州学院学报，2019，33（02）：110-112.
[3]顾春华.中国古书画装裱丝绸纹样仙鹤纹研究[J].武汉纺织大学学报，2019，32（03）：13-17.
[4]李玉霞.论传统书画装裱工艺的演变[J].河南科技学院学报，2016，36（11）：90-92.
[5]欧秀花，安兴龙，沈佳佳，等.蜂蜡在档案修裱浆糊中的应用研究[J].档案管理，2016（05）：37-39.
[6]欧秀花.添加中药对古籍修裱浆糊性能影响的初步研究[J].图书馆杂志，2017，36（09）：52-59.
[7]陈觉声，刘淑贞，刘雄.微波辅助制备醋酸纳米豆渣纤维素工艺研究[J].中国粮油学报，2014，29（07）：96-101.
[8]赵依洋，姜忠丽，代岚，等.糙米酵素糖化液制备工艺优化研究[J].农业科技与装备，2019（05）：35-37.
[9]王国强.中国古籍修复技术体系构建的原则、思路和框架[J].图书馆论坛，2019，39（10）：134-141.
[10]于川.档案与文物修复对比研究——以纸质档案与古籍为例[J].华东纸业，2020，50（02）：1-7.