Amorphous metal-aluminophosphate catalysts for aldol condensation of n-heptanal and benzaldehyde to

来源 :催化学报 | 被引量 : 0次 | 上传用户:ffgooo208w
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
Amorphous aluminophosphate (AlP) and metal‐aluminophosphates (MAlPs, where M=2.5 mol%Cu, Zn, Cr, Fe, Ce, or Zr) were prepared by coprecipitation method. Their surface properties and catalytic activity for the synthesis of jasminaldehyde through the aldol condensation of n‐heptanal and benzaldehyde were investigated. The nitrogen adsorption‐desorption isotherms showed that the microporosity exhibited by the aluminophosphate was changed to a mesoporous and macroporous structure which depended on the metal incorporated, with a concomitant change in the surface area. Temperature‐programmed desorption of NH3 and CO2 revealed that the materials possessed both acidic and basic sites. The acidic strength of the material was either increased or decreased depending on the nature of the metal. The basicity was increased compared to AlP. All the materials were X‐ray amorphous and powder X‐ray diffraction studies indicated the absence of metal oxide phases. The Fourier transform infrared analysis confirmed the presence of phosphate groups and also the absence of any M‐O moieties in the materials. The selected organic reaction occurred only in the presence of the AlP and MAlPs. The selectivity for the jasminaldehyde product was up to 75%with a yield of 65%. The best conversion of n‐heptanal with a high selectivity to jasminaldehyde was obtained with FeAlP as the catalyst, and this material was characterized to have less weak acid sites and more basic sites.
其他文献
利用辐照还原法在500 kGy辐照剂量下制备了Au掺杂MF有机气凝胶.通过X射线衍射(XRD)、能量色散光谱仪(EDX)和透射电子显微镜(TEM)测试证实了辐照法成功地制备出Au掺杂MF有机气
研究了粒径10~100 nm的二氧化硅纳米颗粒在非水基液中的表面活性剂辅助分散.结合颗粒表面特定官能团结构,针对性选择了合适的表面活性剂,氢键桥梁作用和长链分子空间位阻作用
目的:检测高尔基体α-甘露糖苷酶II(Golgi α—mannosidaseII,GMⅡ)、E—cadherin和值α-catenin在不同卵巢上皮肿瘤组织和不同转移能力的卵巢癌细胞中的表达。方法:运用免疫组织
为提高铵法脱硫产物的氧化效率,采用气相沿面放电生成的活性氧物质替代强制氧化法中的空气用于氧化亚硫酸铵,考察了沿面放电等离子体装置中的空气流速、温度、湿度及曝气孔的
聚合物纳米复合材料因其优良的介电性能在电介质绝缘领域得到了广泛的应用.为获得性能优良的绝缘纸,将纳米氮化铝(AlN)添加到芳纶1313中.将改性后的绝缘纸进行浸油处理,研究
基于考虑风电预测误差时间相关性的不确定性场景,将能量型储能同时应用于削峰填谷和计划跟踪两种模式,提出了风储联合系统多模式协调优化模型。同时,针对风储联合运行的大规
为更深入地在微观角度上研究变压器绝缘纸老化机理,利用分子动力学仿真,对不同温度下纤维素无定形区的热力学性质进行了研究.结果表明:纤维素无定形区为各向同性弹性材料,其
为进一步揭示槽型空心阴极放电的放电机理,利用流体-亚稳态原子传输模型模拟研究了槽型空心阴极放电等离子体参数的时空分布特性.模拟得到了不同时刻槽型空心阴极放电中电势
为深入研究矿物绝缘油的带电度和油中腐蚀性硫浓度之间的相关性,在120℃条件下对含有不同质量浓度腐蚀性硫的油样进行了一系列开口和闭口热老化实验。对老化油样的带电度、介