The hot deformation behavior of S460ML steel with different Nb contents was investigated by single-pass compression experiment on the Gleeble-1500 thermo-machine simulator at deformation temperatures ranging from 900 to 1200 ℃ and strain rates from 0.1 to
【机 构】
：
Research Institute of Technology of Shougang Group Co.Ltd., Beijing 100043, China
论文部分内容阅读
The hot deformation behavior of S460ML steel with different Nb contents was investigated by single-pass compression experiment on the Gleeble-1500 thermo-machine simulator at deformation temperatures ranging from 900 to 1200 ℃ and strain rates from 0.1 to 5.0 s-1.The critical strain of dynamic recrystallization (DRC) under different conditions was determined by using working hardening rate-strain curves.The relationship between critical strain and peak strain of DRC was discussed.By means of regression analysis method,the hot deformation activation energy of steels and the mathematical model for predicting DRC critical strain were calculated and established,respectively.The results showed that DRC occurred during hot deformation.As the deformation temperature increased and strain rate decreased,the critical strain of DRC decreased.The critical strain (εc) showed linear relationship with peak strain (εp).As Nb content increased,the needed deformation temperature for occurring DRC increased,while the needed strain rate for it decreased.The activation energy for hot deformation of S460ML steel increased with increasing Nb content.
其他文献
Ordered titanium dioxide nanotubes (TiO2NTs) modified with indium tin oxide (ITO) films were obtained via magnetron sputtering,in which ITO plate was used as a target,onto the as-anodized titania support followed by the calcination process.The morphology
The intrinsic relationship between the microstructure evolution and thermal fatigue behavior of a single-crystal cobalt-base superalloy has been investigated.The thermal fatigue tests are performed cyclically between room temperature and 1050 ℃ using V-no
This study presented a quantitative investigation of deformation behavior and dynamic recrystallization of low-alloy high-strength Ni-Cr-Mo-V steels during hot deformation. A series of isothermal compression experiments were performed at temperatures rang
0The effect of peak temperature (Tp) at 200,300,400,500 and 550 ℃ on the microstructural evolution and softening behavior of the simulated heat-affected zone (HAZ) was studied in the 2219-T87 alloy by electron-backscatter diffraction,transmission electron
The fly ash cenosphere/AZ91D composites were successfully prepared and isothermally heat-treated at different temperatures for different time. The effects of semi-solid isothermal heat treatment on the microstructures and damping capacities of fly ash cen
The effect of sample geometry aspect ratio (l/w) on the giant magnetoimpedance (GMI) in Fe67Co18Si11B4 amorphous ribbons was investigated systematically.The GMI profiles were measured as a function of the external magnetic field at different frequencies u
A modified FGH96 superalloy using 0.1 wt％ graphene was successfully prepared using the wet mixing method.The interfacial bonding mechanism between the graphene and the superalloy matrix was characterized using optical microscope,scanning electronic micros
Dynamic and static aging precipitation of Mg17Al12 phases in AZ80 magnesium alloy was studied by multidirectional forging (MDF) with decreasing temperatures from 410 to 300 ℃ and subsequent aging process.The results show that the morphology of the β-Mg17A
A quantitative phase field method of multi-component diffusion-controlled phase transformations coupled with the Kim-Kim-Suzuki model was applied to study the effect of initial particle size distribution (PSD) in 3D and space distribution in 2D on dissolu
This research article explains the removal of methylene blue (MB) and malachite green (MG) from aqueous solution using adsorption/photodegradation activity of ZnO∶Ag/bamboo charcoal (BC) nanocomposite.In addition,the antibacterial studies of the prepared