Study of decomposing carbonyl slag

来源 :中国有色金属学会会刊(英文版) | 被引量 : 0次 | 上传用户:wf136156491
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
A new technology was put forward to deal with the carbonyl slag at low acidity and low oxygen pressure in the kettle.With the orthogonal experiments for analyzing the sequence of four factors and some single factor experiments for the best conditions. The best conditions are used for extracting nickel, cobalt and copper and enriching precious metals: the cupric ion concentration is 5 g/L; and pH=6; the sulfur coefficient is 1.4; the oxygen pressure is 0.08 MPa; the time bubbling oxygen is 20 min;the ratio of liquid to solid is 8:1; the leaching time is 2 h; the heating time is 2.5 h. The leaching rates of nickel and cobalt are more than 98% and that of copper is above 97%. Nickel and cobalt can be separated efficiently from copper and precious metals from the carbonyl slag. Moreover, its leaching liquor has less copper. Nickel and cobalt can be reclaimed only once. During the whole process,the leaching rates of Au and Ag are more than 99.9%, while other precious metals are still in the residue without any loss.
其他文献
Multidoped spinel LiCo0.02La0.01Mn1.97O3.98Cl0.02 was synthesized by solid-state method. The structure and electrochemical performance were characterized by XRD
The valence electron structures of Sr- and Mg-doped LaGaO3 ceramics with different compositions were calculated by Empirical Electron Theory of Solids and Molec
Cerium phosphate powders were synthesized by direct solid liquid reaction of cerium dioxide and phosphate acid at the Ce∶P ratio of 1∶1. Phase-pure and fine g
The WC-10%Co particulate reinforced Cu matrix composite material with a WC-Co:Cu mass ratio of 20:80 was successfully fabricated by selective laser sintering(SL
Polydimethylsiloxane/polymethylacrylate(PDMS/PMA) interpenetratrating polymer networks(IPNs) was fabricated by simultaneous synthesis and characterized by therm
The TiO2 films were prepared on slides by dc reactive magnetron sputtering, then the samples were annealed at 300 ℃,350 ℃,400 ℃,450 ℃,500 ℃ and 550 ℃,resp
本文对内蒙古发展新型工业化做了SWOT(S:优势,W:劣势,O:机遇,T:威胁)分析,指出了自身的优势、劣势以及外部环境带来的机会和威胁,并在此基础上提出了发展新型工业化策略:充分
For further knowledge about the refining performance of AlTiC master alloys, Al5.5Ti0.25C and Al6.5Ti0.5C master alloys containing high Ti and C content were pr
The magnetic microstructures of 2:17 type Sm(Co,Fe,Cu,Zr)z magnets were detected by magnetic force microscopy.Comparing the microstructures of the specimens coa
Arrhenius formula was applied to calculate the apparent activation energy of zincate reaction. The standard electrode potential of all the metal coordinating io