A novel mechano-synthesis method has been elaborated in this work for the design of efficient cobaltbased Fischer-Tropsch catalysts.The process aims to reduce the total number of steps involved in the synthesis of solid catalysts and thus to avoid relevant toxic solutions generated during the catalyst preparation.The mechano-synthesis of the Co/Al2O3 catalyst was processed in a low-energy vibratory micro mill and high energy planetary ball mill.Porous spherical γ-aluminas (1860 μm and 71 μm mean particle diameter) were used in this work as host compounds.Co3O4 (3 μm mean particle diameter) has provided guest particles for mechano-synthesis.The catalysts were characterized by textural (surface area,porosity and particle size) and structural analyses (X-ray diffraction,TPR,SEM-EDX and microprobe).The microprobe images show deposition of Co3O4 on the surface of the alumina and indicated no Co3O4 diffusion inside the alumina pores.SEM-EDX mapping illustrated that cobalt coating tended to occur on surface of rounded shape of cracked alumina fragments.After milling,the crystallite size of Co3O4 decreased to 15 nm from 30 to 50 nm.The TPR profiles indicated very low concentrations of inactive cobalt aluminate mixed compounds which are usually produced during the catalyst preparation by impregnation.In Fischer-Tropsch synthesis,the catalysts prepared using mechano-synthesis methods showed catalytic performance comparable to the catalysts prepared by impregnation.