A multi-deposition multi-annealing technique(MDMA) is introduced into the process of high-k/metal gate MOSFET for the gate last process to effectively reduce the gate leakage and improve the device’s performance. In this paper, we systematically investigate the electrical parameters and the time-dependent dielectric breakdown(TDDB) characteristics of positive channel metal oxide semiconductor(PMOS) under different MDMA process conditions, including the deposition/annealing(D&A) cycles, the D&A time, and the total annealing time. The results show that the increases of the number of D&A cycles(from 1 to 2) and D&A time(from 15 s to 30 s) can contribute to the results that the gate leakage current decreases by about one order of magnitude and that the time to fail(TTF) at 63.2% increases by about several times. However, too many D&A cycles(such as 4 cycles) make the equivalent oxide thickness(EOT) increase by about 1 ?A and the TTF of PMOS worsen. Moreover, different D&A times and numbers of D&A cycles induce different breakdown mechanisms.
A multi-deposition multi-annealing technique (MDMA) is introduced into the process of high-k / metal gate MOSFET for the gate last process to effectively reduce the gate leakage and improve the device’s performance. In this paper, we systematically investigate the electrical parameters and the time-dependent dielectric breakdown (TDDB) characteristics of positive channel metal oxide semiconductor (PMOS) under different MDMA process conditions, including the deposition / annealing (D & A) cycles, the D & A time, and the total annealing time. that the increases of the number of D & A cycles (from 1 to 2) and D & A time (from 15 s to 30 s) contribute to the results that the gate leakage current decreases by about one order of magnitude and that the time to fail ( TTF) at 63.2% increases by about several times. However, too many D & A cycles (such as 4 cycles) make the equivalent oxide thickness (EOT) increase by about 1? A and the TTF of PMOS worsen. numbers of D & A cycles induce different breakdown mechanisms.