采用红外(IR)及非等温差示扫描量热法(DSC)研究了乙烯基酯树脂(VER)及石墨/VER复合体系的固化行为.结果表明:计算所得VER及石墨/VER复合体系的表观活化能Ea分别为46.15和79.8
论文部分内容阅读
采用红外(IR)及非等温差示扫描量热法(DSC)研究了乙烯基酯树脂(VER)及石墨/VER复合体系的固化行为.结果表明:计算所得VER及石墨/VER复合体系的表观活化能Ea分别为46.15和79.82kJ.mol-1;反应级数n分别为0.950和0.951.复合体系中树脂的固化放热量的平均值ΔH比纯VER体系的约降低17%,一定程度上降低了树脂的固化反应程度;复合体系中树脂几乎不存在后固化现象.
The curing behavior of vinyl ester resin (VER) and graphite / VER composite system was investigated by infrared (IR) and non-isothermal differential scanning calorimetry (DSC) .The results showed that the calculated VER and graphite / VER composite system The activation energy Ea was 46.15 and 79.82 kJ · mol-1, respectively, and the reaction orders n were 0.950 and 0.951, respectively. The mean value of ΔH of curing exotherm of resin in the composite system was about 17% lower than that of the pure VER system to a certain extent Reduce the degree of curing reaction of the resin; composite resin almost no post-curing phenomenon.
其他文献
目的认识淋巴结内巨核细胞,并与转移癌鉴别。方法对1例乳腺癌患者腋窝淋巴结内出现的大细胞进行HE形态、免疫组化染色观察并复习文献。结果淋巴结的皮质区及髓质区的窦内及窦
提出一种高效二次变频结构,分两步将中频信号搬移至基带。首先,通过一种将混频器置于滤波器之后的多相滤波宽带数字下变频结构将中频信号搬移至基带附近。然后通过传统的正交
提出一种基于电流模式DC/DC变换器的驱动控制电路。该电路可以与恒流电路结合在一起,用作LED驱动。电路由误差放大器、斜坡信号产生电路、电流采样与叠加电路以及PWM比较器四
方向特征是目前手写体识别中最常用和有效的特征之一.为了减少方向值提取过程中带来的误差,对改进的方向特征(MDF)提出了进一步的改进(MMDF),在方向值提取过程中对方向突变条件进行调整,同时引入半方向归一化线段方向并用二维数组来表示方向值.实验证明采用BP神经网络分类器对手写数字进行识别,与MDF相比,MMDF能同时降低拒识率和提高识别精度.
采用高能球磨法制备超细WC-Co硬质合金。研究了1 390℃真空通Ar常规烧结后再热等静压烧结(HIP),烧结温度1 320℃,80 MPa下保温60 min对WC-Co硬质合金组织和性能的影响。结果
随着CMOS集成电路特征尺寸的不断缩小,特别是在其发展到深亚微米阶段之后,CMOS器件面临着负偏置温度的不稳定性、栅氧化层经时击穿、互连系统的电迁移和热载流子注入等可靠性
为了提高太阳能的利用率,更加高效地开发太阳能资源,提出了软件计算与传感器实时检测太阳光强相结合的控制方法.根据当地的时间、经纬度,得到当天太阳的高度角和方位角,驱动
晚期糖基化终末产物(AGEs)与其受体(RAGE)在糖尿病及其并发症的发生、发展中起重要作用.缺少胞内区的RAGE称为可溶性RAGE(sRAGE).其可阻断配体与RAGE的结合.糖尿病患者sRAGE
针对新型阻变存储器(RRAM)工艺良率不高的问题,提出了一种新型的修复解决方案,该方案基于阻变单元的特殊性能,即初始状态为高阻,经过单元初始化操作过程后转变为低阻。利用这
目的 了解重症监护病房(ICU)患者下呼吸道感染的临床特点和病原菌分布及耐药情况,为临床合理使用抗菌药物提供依据.方法 对2008年1月至2010年8月我院ICU发生下呼吸道感染患者