The characteristics of mc-Si used for solar cells during H2 ambient annealing at 800-1200 ℃ were investigated by means of FTIR and QSSPCD. The results reveal that grain boundaries or defects in mc-Si may facilitate the formation of oxygen precipitates, and the formation of oxygen precipitates has deleterious effect on the lifetime of mc-Si. Decreasing lifetime could result from the formation of new recombination during annealing. Additionally, It is found that hydrogen may facilitate the formation of oxygen precipitates in mc-Si. On the other hand, the diffusion of hydrogen may passivate the defects/boundaries and it is beneficial to the lifetime of mc-Si.
The characteristics of mc-Si used for solar cells during H2 ambient annealing at 800-1200 ° C were investigated by means of FTIR and QSSPCD. The results reveal that grain boundaries or defects in mc-Si may facilitate the formation of oxygen precipitates, and the formation of oxygen precipitates has deleterious effect on the lifetime of mc-Si. Decreasing lifetime could result from the formation of new recombination during annealing. Additionally, It is found that hydrogen may facilitate the formation of oxygen precipitates in mc-Si. hand, the diffusion of hydrogen may passivate the defects / boundaries and it is beneficial to the lifetime of mc-Si.