【摘 要】
:
对含铟废渣进行了固体酸化焙烧水浸提铟的条件试验。考察了焙烧温度、焙烧时间、固体酸用量、浸出液固比等对含铟废渣中铟浸出率的影响。焙烧温度、固体酸用量对铟浸出率有
【机 构】
:
浙江大学化学系,中南工业大学化学系
论文部分内容阅读
对含铟废渣进行了固体酸化焙烧水浸提铟的条件试验。考察了焙烧温度、焙烧时间、固体酸用量、浸出液固比等对含铟废渣中铟浸出率的影响。焙烧温度、固体酸用量对铟浸出率有显著影响,其它条件影响不大。经试验获得下列工艺条件:料酸比(质量比)1∶2,焙烧时间2h,浸出液固比4∶1,浸出时间15h,铟浸出率93%以上。
Indium-containing waste residue was acidified roasting conditions for the extraction of indium. The effects of calcination temperature, calcination time, solid acid content and leachate solidity ratio on the indium leaching rate from indium-containing waste residue were investigated. The calcination temperature and the amount of solid acid have a significant effect on the leaching rate of indium, while other conditions have little effect. The following process conditions were obtained: the ratio of material to acid (mass ratio) was 1: 2, the roasting time was 2h, the leaching solution to solid ratio was 4:1, the leaching time was 1.5 hours and the leaching rate of indium was above 93%.
其他文献
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥
运用相平衡分析的方法,对(Ga,In)As半导体MOVPE生长过程中源物质热分解后的气相物种分压进行了分析,得到了沉积物种的生成率随各生长参数的变化规律,同时对气相物种分压与半导体碳污染的关系也
综述了近几十年来各国对颗粒增强铝基复合材料(PRA)干滑动磨擦性能的研究成果,对影响PRA耐磨性能的因素进行了分析和总结。在铝及其合金中添加硬质陶瓷颗粒可明显提高材料的抗磨损性能
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥
【摘要】 目的:分析面中部骨折单独坚强内固定与联合颌间牵引对咬关系重建的影响。方法:将面中部骨折136例患者分为A组和B组,A组采用坚强内固定联合颌间弹力牵引1~2周,B组采用单独坚强内固定,观察术后咬关系重建的效果。结果:A组68例患者术后咬关系完全恢复66例,占97.06%,B组68例患者咬关系完全恢复58例,占85.29%,两组比较差异有统计学意义(P<0.01),B组优于A组。结论:面中部
对可用于某些金属基复合材料无损检测的一些主要方法进行了介绍和评价,分析了它们的特点和适用性,所涉及的方法有:超声波反射法、速度法、衰减法,软X射线法、工业CT法、声学振动法和
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥