A new series of cellulose-graft-poly(N-isopropylacrylamide)(cellulose-g-PNIPAM) copolymers were prepared by atom transfer radical polymerization(ATRP) of N-isopropylacrylamide monomers from a cellulose-based macro-initiator, which was homogeneously synthesized in an ionic liquid 1-allyl-3-methylimidazolium chloride(Amim Cl). The composition of cellulose-g-PNIPAM copolymers could be adjusted by altering the feeding ratio and reaction time. The resultant copolymers with relatively high content of PNIPAM segments(molar substitution of PNIPAM ? 18.3) were soluble in water at room temperature. Aqueous solutions of cellulose-g-PNIPAM copolymers exhibited clear temperature-sensitive behavior, and their sol-to-gel phase transition properties were investigated by dynamic light scattering(DLS) and UV measurements. Compared with pure PNIPAM, the cellulose-g-PNIPAM copolymers possessed higher lower critical solution temperatures(LCST) in a range from 36.9 ?C to 40.8 ?C, which are close to normal human body temperature, and could be tuned by adjusting the content of PNIPAM segments in copolymers. Spherical structure of cellulose-g-PNIPAM copolymers formed at temperatures above LCST and its morphology was observed by TEM and SEM. These novel cellulose-g-PNIPAM copolymers may be attractive substrates for some biomedical applications, such as drug release and tissue engineering.
A new series of cellulose-graft-poly (N-isopropylacrylamide) (cellulose-g-PNIPAM) copolymers were prepared by atom transfer radical polymerization (ATRP) of N-isopropylacrylamide monomers from a cellulose-based macro-initiator, which was homogeneously synthesized in an ionic liquid 1-allyl-3-methylimidazolium chloride (Amim Cl). The composition of cellulose-g-PNIPAM copolymers could be adjusted by altering the feeding ratio and reaction time. The resultant copolymers with relatively high content of PNIPAM segments Aqueous solutions of cellulose-g-PNIPAM copolymers exhibited clear temperature-sensitive behavior, and their sol-to-gel phase transition properties were investigated by dynamic light scattering (DLS) and UV measurements. Compared with pure PNIPAM, the cellulose-g-PNIPAM copolymer possessed higher lower critical solution temperatures (LCST) in a range from 36.9 ° C to 40.8 ° C, which are close to normal h uman body temperature, and could be tuned by adjusting the content of PNIPAM segments in copolymers. Spherical structure of cellulose-g-PNIPAM copolymers formed at temperatures above LCST and its morphology was observed by TEM and SEM. These novel cellulose-g-PNIPAM copolymers may be attractive substrates for some biomedical applications, such as drug release and tissue engineering.