【摘 要】
：
我厂生产的熔模精铸铝件支架(如图示),材质为ZL102,铸件净重16g,最小壁厚1.5mm。采用水玻璃型壳、氯化铵硬化工艺生产,涂挂6层。由于铸件壁薄,在铸件A处经常出现“浇不到”
论文部分内容阅读
我厂生产的熔模精铸铝件支架(如图示),材质为ZL102,铸件净重16g,最小壁厚1.5mm。采用水玻璃型壳、氯化铵硬化工艺生产,涂挂6层。由于铸件壁薄,在铸件A处经常出现“浇不到”缺陷,造成铸件大量报废,废品率高达70～80％,严重时可达100％。
I plant casting cast aluminum bracket (as shown), made of ZL102, castings net weight 16g, the minimum wall thickness of 1.5mm. The use of water glass shell, ammonium chloride hardening process, Tu linked to 6 layers. Due to the thin wall of the castings, castings often fail to “fail to meet the requirements”, causing a large number of castings to be scrapped. The rejection rate is as high as 70-80% and in severe cases up to 100%.
其他文献
在材料性能试验中,获得分段光滑曲线的连接点为不光滑点,这些不光滑点的某一个座标值所代表的物理量就是该材料的物性参数或叫材料常数,根据数学上分段光滑曲线定义知,在不光
加工铸铁的Widlanit切削材料主要由氮化硅(Si_3N_4)组成。它兼有硬质合金的韧性和氧化物陶瓷材料的热硬性。在加工铸铁时(图),切削速度可超过1000米/分。粗铣时,尽管出现微
Qingdao is well on its way to claiming the title of Sailing City in the post-Olympic era“Good morning and welcome aboard!” On a Friday morning in September, J
在美国经济非常不景气,以及明年预估将有不少王牌级的球员将成为自由球员的双重条件下,对今年成为自由球员的NBA球员来说,这可不是一个很美好的夏天……
This is not a very
我厂生产的C5523大立车往往因立柱导轨产生气孔而报废,通过分析导轨产生气孔的原因,我们采取了相应的措施,消除了气孔,保证了铸件质量,具体方法如下:一、铸件的特点及气孔产
石武客运专线北起石家庄、南至武汉,是北京—广州—深圳—香港客运专线的一部分,总投资1 167.6亿元,正线全长840.7 km于2008年10月正式启动。石武客运专线横跨华北平原和中原
锯切0.5mm 左右的金属板料,可用两块5mm 左右的金属板料或非金属材料(例如木板、硬性塑料板等)与待锯板料一起用台虎钳夹紧,再用锯条(不论粗、中、细齿均可)锯割就可以了。
沉积容矿喷气(SEDEX)贱金属和重晶石矿床的形成是由于上地壳中地壳热驱动大规模热水对流的结果.对流的流体来自海水和孔隙水.由于热量来自上地壳,因而对流随时间的持续而加深
身为联盟内最具天赋、最全能的自由人之一,鹰队的乔·约翰逊(JoeJohnson)似乎总是得不到太多的注目。这样的现象,也许是他出身阿肯色乡间的低调个性造成,又也许是他所属的鹰
上海第三钢铁厂薄板车间原有6座链式加热炉,这些炉子的炉型结构是比较落后的,经过热平衡测试结果表明:该炉子的炉链和炉爪带走热损失严重,空、煤气预热温度低,炉墙绝热差,炉