【摘 要】
：
本文针对我厂转炉氧枪用管出现的瘪塌问题,着重探讨了(φ133×5氧管瘪塌的内在因素,从理论分析入手,并以实践为依据,对φ133×5氧管瘪塌问题作了较详细的理性论述,同时对氧枪
论文部分内容阅读
本文针对我厂转炉氧枪用管出现的瘪塌问题,着重探讨了(φ133×5氧管瘪塌的内在因素,从理论分析入手,并以实践为依据,对φ133×5氧管瘪塌问题作了较详细的理性论述,同时对氧枪安装制作工艺的实践也作了分析。在理性分析及实践考证的基础上,弄清了φ133×5氧管瘪塌症结之所在,进而采取有效技术措施,使其彻底解决。
This article focuses on the collapse of oxygen lance tubes in our factory, and emphatically discusses the internal factors of (φ133 × 5 oxygen tube collapse, starting from the theoretical analysis, and on the basis of practice, the problem of φ133 × 5 oxygen tube collapse Made a more detailed rationale, at the same time, the practice of oxygen gun installation production process was also analyzed.On the basis of rational analysis and practical research, we clarified the location of φ133 × 5 oxygen tube collapse, and then take effective techniques Measures to make it completely resolved.
其他文献
Ｅｘｔｒａａｘｉａｌｃａｖｅｒｎｏｕｓｈｅｍａｎｇｉｏｍａｓａｒｅｒａｒｅｌｅｓｉｏｎｓａｎｄｈａｖｅａｐｒｏｐｅｎｓｉｔｙｔｏｏｃｃｕｒｗｉｔｈｉｎｔｈｅｃａｖｅｒｎｏｕｓｓｉｎｕｓ［１，２～６］．Ｃｌｉｎｉｃａｌｐｒｅｓｅｎｔａｔｉｏｎｓｏｆｃａｖ?
Extraaxial cavernous hemangiomasarerarelesionsandhaveapropensitytooccurwithinthecavernoussinus[1,2～6]. Clinicalpresentations
在毛主席革命路线指引下,经过无产阶级文化大革命和批林批孔运动,我厂广大干部、工人和技术人员,坚持党的基本路线和社会主义建设总路线,深入开展工业学大庆的群众运动,阶级
１９８８年８月至１９９８年１月，我院收治颅脑损伤患者２８４３例，其中发现临床表现隐匿的颅内肿瘤２６例（占０．９１４％，经ＣＴ检查确诊２４例），均经手术及病理证实。现报告如下。１临床资料本组男１７例，女９例；年龄６～５８岁，平均３８岁。伤后至就诊时间１..
(一)我厂顶吹氧气转炉废气产生的规律:顶吹氧气转炉吹炼期产生大量浓褐色烟雾,染污大气,影响周围环境卫生。因此,必须除尘。废气的产生一般有如下的规律:1.炉内产生的废气量
好消息是如今IT解决方案变得越发先进;坏消息是它们也变得更加复杂。所有的复杂性都会让企业付出代价。
The good news is that IT solutions are becoming more advanced t
由于高炉普遍的采用喷吹燃料新技术,实行高温高压操作,风温由过去的1000℃以下提高到1100～1300℃,压力由0.8～1.5kg/cm~2提高到2.0～5.0kg/cm~2 高炉实行强化操作,就必然提出加大
宫古铜冶炼厂投产于1958年,是一座小型企业,主要接受三井金属公司的委托业务进行生产。厂内设鼓风炉两座,转炉三座,烟气送制酸厂生产硫酸。冶炼工艺采用常规流程。
Palace
从贫硫酸盐溶液中提取镍和钴的现行方法是在较高的温度和压力的条件下,用硫化氢沉出镍和钴的硫化物,然后在高温高压下用压煮器将这些硫化物溶解,产出硫酸镍和硫酸钴並
The
在毛主席“鼓足干劲,力争上游,多快好省地建设社会主义”总路线的指引下,我厂于1972年开始生产抗渗碳耐火材料,至今已生产多种型号的抗渗碳耐火材料约18万件,共计900余吨,供
目前大型顶吹氧气转炉的冶炼能力同现代装有碱性炉顶和氧气喷嘴的平炉相比,要高2～3倍。在采用这种高生产率的炼钢方法时,从经济观点来考虑,要尽量限制停炉。为充分利用冶炼设