The enthalpies of formation of the ternary compounds Al4NiY, Al2NiY, Al2Ni6Y3, Al16 Ni3Y, AlNiY, Al3Ni2Y, AlNi8Y3, Al7Ni3Y2, and of the binary comp ounds Al2Y containing nickel and Ni5Y containing aluminum have been determined by high temperature reaction calorimetry. The enthalpy values measured are compared to previously published results where available as well as extended Miedema model predictions. The melting points of the compounds were determined by DTA and X-ray diffraction was used to confirm the crystal structures of the compounds. The enthalpi es of formation of the ternary compounds show a maximum along the 50%Al (mole fr action) section. The ternary compounds appear along lines of constant yttrium content consistent with binary compound solubility extensions.