论文部分内容阅读
Microstructure evolution of a single crystal nickel-base superalloy during heat treatment and tensile creep at1010℃ and 248 MPa for 30h was observed and analyzed. Internal stresses because of lattice mismatch between γ and γphase provided the driving forc