Effect of inclusion on high cycle fatigue response of a powder metallurgy tool steel
【机 构】
:
University
【出 处】
:
中南大学学报(英文版)
【发表日期】
:
2004年期
【基金项目】
:
supported by the National Key Technologies Research and Development Program of China
其他文献
Synthesis and characterization of Y_2O_2S:Eu~(3+), Mg~(2+), Ti~(4+) nanorods via a solvothermal rout
Y_2O_2S:Eu~(3+), Mg~(2+), Ti~(4+) nanorods were prepared by a solvothermal procedure. Rod-like Y(OH)_3 was firstly synthesized by hydro-thermal method to serve
Effects of nitrogen content on structure and electrical properties of nitrogen-doped fluorinated dia
Nitrogen-doped fluorinated diamond-like carbon (FN-DLC) films were prepared on single crystal silicon substrate by radio frequency plasma enhanced chemical vapo
A series of solid solutions Er_2W_(3-x)Mo_xO_(12) (0.5≤x≤2.5) were successfully synthesized by the solid state method.Their crystal structures and negative th
YAG:Ce phosphor was synthesized by a novel simple method, wherein the admixture of three raw materials (Y_2O_3, α-Al_2O_3 and CeO_2) were first acidified by di
Based on practical situation of rare earth industrial chain, production process and rare earth materials that could produce solid wastes on batch were discussed
La_2O_3 and Y_2O_3 co-doped Mo secondary emitters were prepared by three kinds of doping method combined with high temperature plasma sintering. The secondary e
The effect of aging on microstructure of Mg-Zn-Er alloys at 473 K was investigated using hardness measurement, scanning elec-tron microscopy (SEM) and transmiss
Nanostructured yttrium aluminum garnet powders synthesized by co-precipitation method using tetraeth
Tetraethylenepentamine (C_8H_(23)N_5, TEPA) has been used as a novel precipitant to synthesize yttrium aluminum garnet (Y_3Al_5O_(12),YAG) precursor from a mixe
Monometallic catalyst Pt/SAPO-11 was prepared by impregnation method. Bimetallic catalysts LaPt/SAPO-11 or CePt/SAPO-11 was prepared by sequential impregnation
Oxidation behavior of Fe40Al-xWC composite coatings obtained by high-velocity oxygen fuel thermal sp
The Fe40Al-xWC (x=0,10,12,15) coatings with dense structure were successfully deposited by high-velocity oxygen fuel (HVOF) spraying of a mixture of Fe,Al and W