Analyzing raw material’s structure and performance of bentonite from Panzhihua in Sichuan, the authors think that it is adequate for agglomerant of iron smelting. According to its composition and property we have researched the purification and modification of I/S bentonite under conditions of different dispersants and sodium agent. XRD test result reveals that the essential minerals of Panzhihua bentonite are I/S mixed-layer ones, and FTIR analysis shows that when adding 1.5% sodium pyrophosphate to the bentonite slurry during purification, the composition of quartz in bentonite decreases to less than 4% and I/S is more than 90%. The optimized modification technic conditions are Na2CO3 (4%) and CMC-Na (3%) as modified agents, the clay and water are 10 vs. 1, and the temperature is 75℃. It is 40 min for stirring time and reacting time is 4 h. Under the conditions we can get the modified I/S bentonite with colloid index more than 500 ml/15 g.
Analyzing raw material’s structure and performance of bentonite from Panzhihua in Sichuan, the authors think that it is adequate for agglomerant of iron smelting. According to its composition and property we have researched the purification and modification of I / S bentonite under conditions of different dispersants and sodium agent. XRD test result reveals that the essential minerals of Panzhihua bentonite are I / S mixed-layer ones, and FTIR analysis shows that when adding 1.5% sodium pyrophosphate to the bentonite slurry during purification, the composition of quartz in bentonite decreases to less than 4% and I / S is more than 90%. The optimized modification technic conditions are Na2CO3 (4%) and CMC-Na 75 ° C. It is 40 min for stirring time and reacting time is 4 h. Under the conditions we can get the modified I / S bentonite with colloid index more than 500 ml / 15 g.