Mechanistic Investigation into the Role of Aluminum Diffusion in the Oxidation Behavior of Cryomille
【机 构】
:
Department of Chemical Engineering and Materials Science, University of California Davis, Davis, CA,
【出 处】
:
武汉理工大学学报(材料科学版)(英文版)
【发表日期】
:
2016年1期
其他文献
Nitrogen-doped Porous Carbon Derived from Surface-attached Polymer Layers for Oxygen Reduction React
We reported the synthesis of nitrogen-doped carbon using surface-attached polyelectrolyte layers as precursors. The synthesized material has a large surface area of 800 m2·g-1 with uniformed pore distribution. Benefitfed from the high pyridinic nitrogen c
Porous Fe-Si alloys with different nominal compositions ranging from Fe-10wt% Si to Fe-50wt% Si were fabricated through a reactive synthesis of Fe and Si elemental powder mixtures. The effects of Si contents on the pore structure of porous Fe-Si alloy wer
Hydroxyl terminated polybutadiene (HTPB) based polyurethane (PU)-polystyrene (PS) interpenetrating polymer network (IPN) was prepared and characterized by FTIR, TGA, WCA, swelling experiments, and SEM. The IPN was used for pervaporation (PV) recovery of b
Effect of Oxygen Partial Pressure on Epitaxial Growth and Properties of Laser-Ablated AZO Thin Films
SPES/PVDF blends were employed to prepare the ion exchange membranes for vanadium redox flow battery (VRB) application for the first time. The addition of the highly crystalline and hydrophobic PVDF effectively limited the swelling behavior of SPES. The v
Plasma electrolytic oxidation (PEO) coatings were prepared on AZ31 magnesium alloy using alkaline phosphate as base electrolyte system, and with the addition of sodium silicate (Na2SiO3), sodium aluminate (NaAlO2) and potassium fluorozirconate (K2ZrF6) as
Optimisation of Bio-polyol Production from Cassava Residue Using Ethylene Glycol as the Liquefaction
Cassava residue was liquefied by using ethylene glycol (EG),ethylene carbonate,propylene carbonate and polyethylene glycol (molecular weight:400 g/mol) as the liquefaction reagent respectively at the temperature of 130-170 ℃ with sulfuric acid as the cata
Effect of Steel Slag and Granulated Blast-furnace Slag on the Mechanical Strength and Pore Structure
Reuse of solid industrial wastes is an effective approach to develop low-carbon construction materials.This paper examines how two materials,steel slag(ST)and granulated blast-furnace slag(SL)impact the mechanical performance and pore structure of cement-