【摘 要】
：
The paper comprises new analytical data on the nature and occurrence of gold in solid pyrobitumen,closely associated with the main gold-bearing sulfide arsenic ores of the Bakyrchik gold deposit (Kazakhstan),related to post-collisional magmatic-hydrotherm
【机 构】
：
Department of Mineralogy and Petrography,Institute of Mineralogy and Geology,Faculty of Earth Scienc
论文部分内容阅读
The paper comprises new analytical data on the nature and occurrence of gold in solid pyrobitumen,closely associated with the main gold-bearing sulfide arsenic ores of the Bakyrchik gold deposit (Kazakhstan),related to post-collisional magmatic-hydrothermal origin.Gold min-eralization of the deposit occurs mainly in the form of an“invisible” type of gold in the structures of arsenian pyrite and arsenopyrite,and the form of gold-organic compounds of pyrobitumen in carbonaceous-terrigenous sequences of Carboniferous formation.Microscopic and electron microscopic analysis,Raman and FT-Infrared analysis,mineralogical and three-step sequential extraction analysis(NH2OH·HCl,H2O2,HNO3 + HCl) has been carried out using 9 ore samples (from 3 different types of ores) for a comprehensive study of pyrobitumen and sulfide arsenic ores focusing mainly on organic matter.The sequentially extracted precious metal content of pyrobitumen reaches up to 7 ppm gold and other metals like Ag 4 ppm,Pt 31 ppb,and Pd 26 ppb,forming metal-organic com-pounds,while arsenic sulfide minerals incorporate 11 ppm gold,39 ppm Ag,0.49 ppm Pt.The enrichment of gold associating with organic matter and sulfide ore minerals was confirmed in this study.Organic matter was active in the migration of gold and the capture of gold by pyrobi-tumen.Moreover,the reductive organic matter agent released gold,most likely for the sulfide arsenic ore min-erals.Pyrobitumen was a decisive factor in the concen-tration,transportation,and preservation of gold in the deposit.
其他文献
This paper seeks to identify macroscopic met-allogenic mechanisms of various mineral deposits by studying microscopic typomorphic characteristics of typi-cal minerals associated with the deposits and to reveal the mechanism of lattice gold in detail by st
The volcanic rocks of the Colíder and Roosevelt formations are extensively exposed in the south-central portion of the Amazonian Craton where effusive and pyroclastic rocks have been mapped.Both units,topped by chemical sediments and oceanic facies as rhy
为解决相变材料聚乙二醇单甲醚(MPEG)在使用过程中存在易泄漏和导热系数低的问题,采用化学和物理相结合的方法制备了一种以海绵状氧化石墨烯(SG)为载体的定形相变材料FSPCM.利用红外光谱仪、拉曼光谱仪、差示扫描量热仪、热台和导热系数仪对FSPCM的化学结构、相变性能、高温热定形效果进行测试.结果表明:MPEG通过物理吸附和酯化反应成功负载到SG上,当FSPCM中SG的质量分数为6％ 时,其相变温度为37.5℃,熔融焓为129.7 J/g,焓值效率高达95.2％,且在250℃时仍具有较好的高温热定形效果.
Chromosomes are well-organized carriers of genetic information in eukaryotes and are usually quite long,carrying hundreds and thousands of genes.Intriguingly,a clade of single-celled ciliates,Spirotrichea,feature nanochromosomes—also called “gene-sized ch
开发可应对耐药菌感染的创面敷料成为医用纺织领域的研究重点之一.采用静电纺丝技术,将聚乙烯醇(PVA)和海藻酸钠(SA)按不同质量比共混纺丝,随SA质量分数的增加,混纺纤维膜力学性能呈下降趋势.优选力学性能较好的混纺纤维膜涂覆ε-聚赖氨酸(ε-PL),因混纺膜中具有水溶性的PVA遇水溶解可释放出抗菌药物ε-PL,且PVA可与SA交联产生缓释效应.通过扫描电子显微镜、强力仪、红外光谱仪及抗菌试验对混纺膜的微观形貌、力学性能、表面化学成分及抗菌性能等进行表征.结果表明,ε-PL被成功负载于混纺纤维膜中,混纺膜耐
炭纸是燃料电池膜电极组件中的关键材料,起到气、液、电、热传输以及支撑催化层的作用.为研究炭纸自身孔结构对其性能的影响,采用湿法成纸和混抄不同长径比炭纤维的方法制备具有不同孔结构的炭纸,并对炭纸的表面形貌、结构和性能进行表征.结果表明:单种长径比炭纤维制成的炭纸,其厚度、面内电阻率、树脂炭质量分数和表面水接触角随炭纤维长径比提升而降低,其法向电阻率与拉伸强度随炭纤维长径比提升而增加;采用长径比值分别为571和857的CF4和CF6混抄得到的炭纸,随CF6质量分数增加,其厚度、面内电阻率、树脂炭质量分数和表面
利用一步化学还原法将二硫化钼(MoS2)纳米花嵌入石墨烯中,制得一种多孔的光热复合水凝胶,即二硫化钼夹层石墨烯水凝胶,其与人工蒸腾装置相结合用于构筑太阳能驱动的界面水蒸发体系.通过扫描电镜、透射电镜、X射线粉末衍射仪、紫外可见-近红外分光光度计及红外热像仪测试材料的形貌和理化性能,并将复合水凝胶置于模拟太阳光下进行水蒸发及脱盐试验.结果表明:MoS2能稳定分散在石墨烯纳米片中,且二者的结合有助于增强材料的光热性能.结合人工蒸腾装置的特殊热定位和快速补水优势,该光热体系能够实现水的快速蒸发,在3.6 kW/
为确定叶型沸石咪唑酯骨架(ZIF)材料ZIF-L在聚丙烯腈(PAN)纳米纤维膜上的最佳生长时间,并探究预氧化处理对PAN纳米纤维膜和ZIF-L/PAN复合纤维膜结构的影响,采用静电纺丝技术制得PAN纳米纤维膜,并通过浸泡法在其上生长ZIF-L晶体,制得ZIF-L/PAN复合纤维膜.对PAN纳米纤维膜及ZIF-L/PAN复合纤维膜进行230～300℃的预氧化处理,并对预氧化前后的PAN纳米纤维膜及ZIF-L/PAN复合纤维膜的表观形貌、红外光谱和热重分析进行测试.结果表明:预氧化处理会使PAN纳米纤维膜上的
黄化机搅拌轴是黏胶纤维原液生产中的关键部件,其主轴与支撑臂采用Q345钢焊接在一起,因搅拌过程中承受较大交变载荷,一定工作循环后焊接处的早期微裂纹会扩展成裂缝,致使搅拌轴过早失效返修.对黄化机搅拌轴进行有限元分析,并对焊接处易出现裂纹的部位进行缺陷检测,分析得出:应力集中和焊接缺陷是造成搅拌轴疲劳破坏或断裂失效的主要原因.采用容许应力幅法和裂纹扩展寿命估算法分别计算搅拌轴无、有初始焊接裂纹缺陷两种情况下的寿命,结果表明:在无初始焊接裂纹缺陷的情况下,搅拌轴寿命至少有10年;在有初始焊接裂纹缺陷的情况下,搅
In the last five decades,Rare Earth Elements(REE) are mostly produced from carbonatite complexes and alkaline magmatic environments.In this respect,pyroclastic flows produced by the potassic-alkaline G(o)lcüik volcanism in the Isparta (SW,Turkey) angle st