To investigate the bacterial colonization on zirconium oxide and titanium surfaces in vivo quantitatively using a confocal laser scanning microscope (CLSM). Ten samples of zirconium oxide ceramic and commercially pure titanium were fabricated and polished using silicon carbide abrasive paper. One sample from each group was evaluated topographic pattern under a scanning electron microscope. One sample from each group was to evaluate roughness using a profilometer. Eight volunteers were selected. The samples were cemented at the buccal surfaces of upper first molars. All samples were removed after 48 hours, immersed in SYTO-9 and propidium iodide fluorescent to stain for adherent bacteria and observed with CLSM. Fewer bacteria were observed in zirconia group than titanium group. However, there was no statistical difference between two groups. The experimental results demonstrate that zirconium oxide may be considered as a promising material for dental implant abutments.
To investigate the bacterial colonization on zirconium oxide and titanium surfaces in vivo quantitatively using a confocal laser scanning microscope (CLSM). Ten samples of zirconium oxide ceramic and commercially pure titanium were fabricated and polished using silicon carbide abrasive paper. One sample from each group was Both volunteers were selected. The samples were cemented at the buccal surfaces of upper first molars. All samples were removed after 48 hours, immersed in SYTO-9 and propidium iodide fluorescent to stain for adherent bacteria and observed with CLSM. However, there was no statistical difference between two groups. The experimental results demonstrate that zirconium oxide may be considered as a promising material for dental implant abutments.