Morphology and Mechanical Characteristics of Monolayer and Multilayer Ir Coating by Double Glow Plas
【机 构】
：
School of Mechanical Engineering, Changzhou University, Changzhou 213164, China;College of Material
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
【发表日期】
：
2017年1期
其他文献
SiC reinforced graphite composites were prepared via introducing carbide silicon into the natural graphite flakes (NGF) by hot-pressing process. Their physical and mechanical properties, including density, open porosity, flexural strength, and friction be
Synthesis of Metal/Poly(diphenylsilylenemethylene) Nanocomposite Thin Films by Pulsed Laser Ablation
Generation Mechanism of Interfacial Layer and Its Effect on Fe-Cr-Ni/Al-Si-Cu-Ni-Mg Composite Perfor
Fe-Cr-Ni/Al-Si-Cu-Ni-Mg composite was taken as the experimental material. The chemical composition of interfacial layer was tested. The generation mechanism and influence of interfacial layer on the composite were analyzed. The results indicated that the
Effects of Aging Temperature on Microstructure and High Cycle Fatigue Performance of 7075 Aluminum A
The hardness,the tensile and the high-cycle fatigue (HCF) performances of 7075 aluminum alloy were investigated under temper T651,solution treated at 380 ℃ for 0.5 h and aged at different temperatures (150,170,190 ℃) for 10 hours.The optimal microstructur
Preparation and Evaluation of Insulin-loaded Nanoparticles based on Hydroxypropyl-β-cyclodextrin Mod
Preparation and Evaluation of an Injectable Chitosan-Hyaluronic Acid hydrogel for Peripheral Nerve R
Effects of Biaxial Tensile on the Deformation Behavior of DP590 High-strength Steel Sheet under High
The effects of biaxial tensile pre-strain on the forming limit of DP590 high-strength steel under high strain rate were investigated. The stress-strain curves of DP590 steel sheet under the biaxial tensile of different load ratios were obtained. The formi
The Mg/MoS2 composites were prepared by ball milling under argon atmosphere, and the effect of MoS2 on the crystal structure and hydrogen storage properties of Mg was investigated. It is found that 10 wt% of MoS2 is sufifcient to prevent particle aggregat
Cu-Al-O Nanofi bers Fabricated by Electrospinning and Their Ozone Sensing Properties at Room Tempera
Cu-Al-O nanofibers are synthesized by an electrospinning method. After electrospinning process, these nanofi bers were thermally treated at different temperatures from 900 to 1 100?. The morphology and crystal structure of thefi bers were analyzed by scan