The crystallization behavior of melt-sp un Nd8.5Fe78Co5Cu1Nb1B6.5 ribbons was investigated using dynamic differential scanning calorimetry (DSC) and X-ray diffr
The oxidation behavior of Ni-Cr-Al-Y coating produced by multi-arc ion plating with and without an enamel coating was investigated in flow oxygen and oxygen con