【摘 要】
:
Cu47Ti34Zr11Ni8,(Cu47Ti34Zr11Ni8)99Si and (Cu47Ti34Zr11Ni8)99Al bulk metallic glass were prepared by copper mold casting method,and the thermal stability,mechan
【机 构】
:
Department of Materials Science and Engineering
论文部分内容阅读
Cu47Ti34Zr11Ni8,(Cu47Ti34Zr11Ni8)99Si and (Cu47Ti34Zr11Ni8)99Al bulk metallic glass were prepared by copper mold casting method,and the thermal stability,mechanical properties and microstructures of them were studied. With minor alloying of Si and Al additions,the glass transition temperature (Tg),crystallization temperature (Tx1) and temperature interval of supercooled liquid region -Tx (=Tx1-Tg) and reduced glass transition temperature (Trg) were proved to be changed from 672 K,734 K,62 K,0.575 to 691 K,752 K,61 K,0.592 and to 681 K,729 K,48 K,0.590,respectively. The results indicate that the glass-forming ability (GFA) are improved with minor alloying additions. And the bulk glasses also exhibits high three point-bending flexural strength. Because of the additions of Si and Al,three point-bending flexural strength and flexural modulus of the bulk glass change from 2 350 MPa,102 GPa to 3 260 MPa,102 GPa and 2 970 MPa,108GPa respectively. The obvious strengthening is due to the appearance of the medium-range ordered regions with a size of 2-5 nm under the high-resolution TEM image. The reason that the mixed amorphous and nanocrystalline phases caused by minor alloying of Si and Al additions,is that Si or Al is the third kind of elements,which are different from other constituting elements,and there are a strong bonding and atoms size effects between constituting elements,which cause the glass-forming ability (GFA) and the bulk metallic glasses strength improving.
其他文献
The preparation technics of glass-ceramics with super low coefficient of thermal expansion containing β-quartz solid solution as a main crystal phase based on
Optically transparent alumina ceramics were fabricated by conventional process and sintered without pressure in H2 atmosphere. The results indicate that relativ
The chemical vapor(CVD) deposition-diffusion method was applied to prepare FeSi alloys with high silicon content up to 6.5%. In spite of various deposition and
Using embedded-atom-method potential for Pd and MORSE potential for the interaction between H and Pd atoms,the adsorption properties of H atoms on Pd (211),(311
The highly pure nano-crystal Mg,Al-hydrotalcite with titania doping was synthesized by one-step liquid reaction method at atmospheric pressure. The preparation
Solvothermal technique, an one-step soft solution-processing route was successfully employed to synthesize single crystalline CdS nanowires in ethylenediamine m
The effect of cooling rate on the solidification process of Al-2.06%Si-1.58%Mg was numerically and experimentally investigated. The solidification paths and the
The aluminium tubes with high strength and smooth outer-surface can be produced by non-mandrel drawing process. It is an effective method to study forming mecha
Electrical conductivities of micron-scale aluminum wires were quantitatively measured by a four-point atomic force microscope (AFM) probe. This technique is a c
BiFeO3 (BFO) thin films were prepared on Pt(111)/TiO2/SiO2/Si(100) substrates by the pulsed-laser deposition (PLD) technique at a low temperature of 450℃. The