Fe/Si3N4 composite powder was synthesized by the heterogeneous precipitation-thermal reduction process,and then pressed into flakes under a pressure of 10 MPa.Flakes were sintered by pressureless and hot-pressing at 1 600℃under 0.1 MPa N2. The chemical co